Na+とMg2+の協同ドーピングによるLiリッチLi_1.2Ni_0.13Co_0.13Mn_0.54O_2の電気化学的性能の改善【JST・京大機械翻訳】

Improving the electrochemical performances of Li-rich Li_1.2Ni_0.13Co_0.13Mn_0.54O₂ through cooperative doping of Na⁺ and Mg²⁺

著者 (17件)： Sun Yanxia (Key Laboratory of Comprehensive and Highly Efficient Utilization of Salt Lake Resources, Qinghai Institute of Salt Lakes, Chinese Academy of Sciences, Xining 810008, China) ,  Sun Yanxia (Key Laboratory of Salt Lake Resources Chemistry of Qinghai Province, Xining 810008, China) ,  Zhang Lijuan (College of Chemistry and Chemical Engineering, Qinghai University for Nationalities, Xining, Qinghai 810007, China) ,  Dong Shengde (Key Laboratory of Comprehensive and Highly Efficient Utilization of Salt Lake Resources, Qinghai Institute of Salt Lakes, Chinese Academy of Sciences, Xining 810008, China) ,  Dong Shengde (Key Laboratory of Salt Lake Resources Chemistry of Qinghai Province, Xining 810008, China) ,  Zeng Jinbo (Key Laboratory of Comprehensive and Highly Efficient Utilization of Salt Lake Resources, Qinghai Institute of Salt Lakes, Chinese Academy of Sciences, Xining 810008, China) ,  Zeng Jinbo (Key Laboratory of Salt Lake Resources Chemistry of Qinghai Province, Xining 810008, China) ,  Shen Yue (Key Laboratory of Comprehensive and Highly Efficient Utilization of Salt Lake Resources, Qinghai Institute of Salt Lakes, Chinese Academy of Sciences, Xining 810008, China) ,  Shen Yue (Key Laboratory of Salt Lake Resources Chemistry of Qinghai Province, Xining 810008, China) ,  Li Xiang (Key Laboratory of Comprehensive and Highly Efficient Utilization of Salt Lake Resources, Qinghai Institute of Salt Lakes, Chinese Academy of Sciences, Xining 810008, China) ,  Li Xiang (Key Laboratory of Salt Lake Resources Chemistry of Qinghai Province, Xining 810008, China) ,  Ren Xiufeng (Key Laboratory of Comprehensive and Highly Efficient Utilization of Salt Lake Resources, Qinghai Institute of Salt Lakes, Chinese Academy of Sciences, Xining 810008, China) ,  Ren Xiufeng (Key Laboratory of Salt Lake Resources Chemistry of Qinghai Province, Xining 810008, China) ,  Ma Luxiang (College of Materials and Chemistry and Chemical Engineering, Chengdu University of Technology, Chengdu, Sichuan 610059, China) ,  Hai Chunxi (Key Laboratory of Comprehensive and Highly Efficient Utilization of Salt Lake Resources, Qinghai Institute of Salt Lakes, Chinese Academy of Sciences, Xining 810008, China) ,  Hai Chunxi (Key Laboratory of Salt Lake Resources Chemistry of Qinghai Province, Xining 810008, China) ,  Zhou Yuan (College of Materials and Chemistry and Chemical Engineering, Chengdu University of Technology, Chengdu, Sichuan 610059, China)
資料名： Electrochimica Acta  (Electrochimica Acta)
巻： 414  ページ： Null  発行年： 2022年 
JST資料番号： B0535B  ISSN： 0013-4686  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： 高容量カソードにはリチウムリッチマンガン系酸化物が含まれる。ここでは,弱いサイクル性能と貧弱なレート容量を克服するために,リチウムリッチマンガン系酸化物ミクロスフェアに,ある量のMgとNaを導入した。本研究では,ドーパントとして高温固相法及びCH_3COONa及びC_4H_14MgO_8と組み合わせた水熱法を用いた。透過電子顕微鏡(TEM),X線回折(XRD),集束イオンビーム走査型電子顕微鏡(FIB-SEM),エネルギー分散分光(EDS),X線光電子分光法(XPS),および電気化学的キャラクタリゼーションを行い,Li_1.2Ni_0.13Co_0.13Mn_0.54O_2の形態,構造および電気化学特性に及ぼすNaおよびMg元素ドーピングの影響を系統的に評価した。結果は,材料が優れた電気化学的性能を有することを示した。これらの改善は,Li層中のNaの存在とTM層中のMgの存在に関連し,Liイオン拡散速度を上げ,イオンおよび電子伝導率を改善することができた。DFT計算は,NaとMgの注入がリチウムイオン移動障壁エネルギーを減少させることを示した。この二重ドープ修飾技術は,LIB用の高容量で安定なカソード材料をいかに構築するかを理解するのに役立つ。Copyright 2022 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： X線回折 ,  高温 ,  *ナトリウム ,  *マグネシウム ,  マンガン ,  *リチウム ,  酸化物 ,  *ドーピング ,  イオン拡散 ,  リチウム化合物 ,  *電気化学 ,  固相 ,  ドーパント ,  密度汎関数法 ,  金属イオン ,  カソード
準シソーラス用語： リチウムイオン , 【Automatic Indexing@JST】

著者キーワード (4件)： 混合ドーピング改質 ,  Liリッチなマンガン系酸化物 ,  電気化学性能 ,  DFT計算

分類 (2件)： 二次電池  (YB04030K) ,  電気化学反応  (CB07050F)

タイトルに関連する用語 (4件)： 協同 ,  ドーピング ,  Li ,  電気化学的性能