転炉製鋼プロセスにおけるノズルねじれランスブローイングによる多相流特性の変化【JST・京大機械翻訳】

Variation in Multiphase Flow Characteristics by Nozzle-Twisted Lance Blowing in Converter Steelmaking Process

著者 (6件)： Lv Ming (School of Metallurgical Engineering, Xi’an University of Architecture and Technology, Xi’an, 710055, China) ,  Li Hang (School of Metallurgical Engineering, Xi’an University of Architecture and Technology, Xi’an, 710055, China) ,  Xing Xiangdong (School of Metallurgical Engineering, Xi’an University of Architecture and Technology, Xi’an, 710055, China) ,  Lin Tengchang (Institute for Metallurgical Process, Central Iron and Steel Research Institute, Beijing, 100081, China) ,  Hu Shaoyan (School of Iron and Steel, Soochow University, Suzhou, 215137, China) ,  Xie Kun (School of Metallurgical Engineering, Xi’an University of Architecture and Technology, Xi’an, 710055, China)
資料名： Steel Research International  (Steel Research International)
巻： 93  号： 2  ページ： e2100409  発行年： 2022年 
JST資料番号： A0446A  ISSN： 1611-3683  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： ドイツ (DEU)  言語： 英語 (EN)

抄録/ポイント： ノズルねじりランスを有する120t変換器のための3Dガススラグ-金属モデルを確立し,そして,ガスジェット特性,スラグ-金属界面変動,壁浸食,および吹出工程のノズルねじりランスの溶融プール流れ場における変化を研究した。その結果,旋回角の増加とともに,噴流高速度断面の長さ,最大速度,および動的圧力減少,半径方向距離は増加し,そして,壁剪断応力は,最初に減少し,次に増加した。吹出時間の増加とともに,スラグ表面および溶鋼表面の変動強度は,著しく変化し,そして,1.7秒(変動強度1.08~1.12)後に,変動スラグ表面は安定化し,そして,1.3秒(変動強度1.23~1.33)後に,変動する鋼表面は,安定化した。ガススラグ-金属三相相互作用領域の乱流運動エネルギーは増加し,壁せん断応力は徐々に増加した。Copyright 2022 Wiley Publishing Japan K.K. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： 界面 ,  相互作用 ,  ねじり ,  *ノズル ,  *混相流 ,  スラグ ,  *鋼 ,  溶鋼 ,  *ランス ,  溶融池 ,  吹出 ,  モデル ,  三次元 ,  動圧 ,  流れ場

著者キーワード (5件)： 転炉製鋼 ,  流れ場の分布 ,  スラグ-金属界面のゆらぎ ,  ノズルねじれランス ,  壁浸食