ポリウレタン表面の炭素析出とアルゴン後処理:構造-機械的および破壊特性【JST・京大機械翻訳】

Carbon deposition and argon post-treatment of polyurethane surface: Structural-mechanical and fracture properties

著者 (7件)： Morozov Ilya A. (Institute of Continuous Media Mechanics UB RAS, Academika Koroleva st. 1, 614013 Perm, Russia) ,  Kamenetskikh Alexander S. (Institute of Electrophysics UB RAS, Amundsen st. 106, 620016 Ekaterinburg, Russia) ,  Beliaev Anton Y. (Institute of Continuous Media Mechanics UB RAS, Academika Koroleva st. 1, 614013 Perm, Russia) ,  Izumov Roman I. (Institute of Continuous Media Mechanics UB RAS, Academika Koroleva st. 1, 614013 Perm, Russia) ,  Bannikov Mikhail V. (Institute of Continuous Media Mechanics UB RAS, Academika Koroleva st. 1, 614013 Perm, Russia) ,  Scherban Marina G. (Perm State University, Bukireva st. 15, 614990 Perm, Russia) ,  Kiselkov Dmitriy M. (Institute of Technical Chemistry UB RAS, Academika Koroleva st. 3, 614013 Perm, Russia)
資料名： Surface & Coatings Technology  (Surface & Coatings Technology)
巻： 437  ページ： Null  発行年： 2022年 
JST資料番号： D0205C  ISSN： 0257-8972  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： プラズマイオンによる高分子表面の改質は,柔軟な機能性材料を作る際に展望を持つ。それらの変形挙動は,破壊抵抗がすべての利点を相殺するので,最も重要な特性の一つである。炭素イオンは,その後のアルゴン処理により弾性ポリウレタンの表面に析出した。生成炭素含有ナノ層は濡れ性と不均一局所機械的性質を増加させた。歪>100%の単軸伸長は炭素改質表面の不連続微小亀裂を誘起するが,それらの伝播は改質層の不均一性によって制約される。Argon後処理は濡れ性をさらに改善するが,破壊抵抗を低下させる局所機械的性質を均一にする。50%までの多サイクル単軸荷重は,表面を損傷しないが,改質層では,破壊の前駆体を弱くする。これは,歪>100%の亀裂抵抗を改善し,不規則微小亀裂のメッシュが長い亀裂の伝播を妨げるように見える。Copyright 2022 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： イオン ,  亀裂 ,  プラズマ ,  濡れ ,  *アルゴン ,  *炭素 ,  *ポリウレタン ,  弾性 ,  高分子 ,  破壊強さ ,  前駆体 ,  不連続性 ,  耐亀裂性 ,  微小亀裂
準シソーラス用語： ナノ薄膜 , 【Automatic Indexing@JST】

著者キーワード (5件)： ポリウレタン ,  炭素沈着 ,  Argon治療 ,  破壊抵抗 ,  疲労荷重

分類 (2件)： 医用素材  (GA05040H) ,  その他の表面処理  (WC08070F)

タイトルに関連する用語 (4件)： ポリウレタン ,  炭素析出 ,  アルゴン ,  破壊特性