アルミナセラミックの焼結性を強化するための水支援冷間静水圧プレス【JST・京大機械翻訳】

Water-assisted cold isostatic pressing to enhance sinterability of alumina ceramics

著者 (5件)： Kermani Milad (Key Laboratory of Advanced Technologies of Materials, Ministry of Education, School of Materials Science and Engineering, Southwest Jiaotong University, Chengdu, China) ,  Pouchly Vaclav (CEITEC BUT, Brno University of Technology, Brno, Czech Republic) ,  Lin Yong (Key Laboratory of Advanced Technologies of Materials, Ministry of Education, School of Materials Science and Engineering, Southwest Jiaotong University, Chengdu, China) ,  Hu Chunfeng (Key Laboratory of Advanced Technologies of Materials, Ministry of Education, School of Materials Science and Engineering, Southwest Jiaotong University, Chengdu, China) ,  Grasso Salvatore (Key Laboratory of Advanced Technologies of Materials, Ministry of Education, School of Materials Science and Engineering, Southwest Jiaotong University, Chengdu, China)
資料名： International Journal of Applied Ceramic Technology  (International Journal of Applied Ceramic Technology)
巻： 19  号： 3  ページ： 1249-1254  発行年： 2022年 
JST資料番号： W1929A  ISSN： 1546-542X  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： アメリカ合衆国 (USA)  言語： 英語 (EN)

抄録/ポイント： 水支援冷間静水圧プレス(WAP)は,微細粒(0.6μm)の常圧焼結とほぼ完全緻密(99.3%)弱半透明アルミナセラミックを可能にした。比較として,同一処理条件下で調製した乾燥プレス(DP)試料は不透明外観を維持し,それらの相対密度は97.7%を超えなかった。WAPの圧密強化は焼結温度を1350°Cまで下げることができ,これはDP粉末より約100~150°C低かった。WAP試料は,焼結(640kJ/mol)整合文献値に対する見かけの活性化エネルギーをもたらし,焼結機構の変化よりむしろ,焼結性の向上が,改善されたグリーン密度に起因することを確認した。Copyright 2022 Wiley Publishing Japan K.K. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： 圧密 ,  *焼結 ,  密度 ,  粉体 ,  *アルミナ ,  *焼結性 ,  *静水圧 ,  相対密度 ,  加熱温度
準シソーラス用語： 半透明 ,  *アルミナセラミック ,  焼結温度 ,  低温焼結 ,  常圧焼結 ,  見掛活性化エネルギー , 【Automatic Indexing@JST】

著者キーワード (3件)： アルミナ ,  グリーン密度 ,  低温焼結

分類 (1件)： セラミック・陶磁器の製造  (YC03020V)

タイトルに関連する用語 (7件)： アルミナセラミック ,  焼結性 ,  強化 ,  水 ,  支援 ,  静水圧 ,  プレス