一次Mnリッチ相に対するAl-Si-Cu-Mn-Ni耐熱合金におけるBと不純物元素の微量添加の精錬効果【JST・京大機械翻訳】

Refining effect of trace addition of B and the impurity elements in Al-Si-Cu-Mn-Ni heat-resistant alloy on primary Mn-rich phase

著者 (5件)： Li Guangjing (School of Materials Science and Engineering, Southeast University, Jiangsu Key Laboratory for Advanced Metallic Materials, Nanjing 211189, China) ,  Liao Hengcheng (School of Materials Science and Engineering, Southeast University, Jiangsu Key Laboratory for Advanced Metallic Materials, Nanjing 211189, China) ,  Teng Huaijin (School of Materials Science and Engineering, Southeast University, Jiangsu Key Laboratory for Advanced Metallic Materials, Nanjing 211189, China) ,  Yang Linlong (Suzhou Mingzhi Technology Co., Ltd., Suzhou 215216, China) ,  Guo Huiting (Suzhou Mingzhi Technology Co., Ltd., Suzhou 215216, China)
資料名： Materials Letters  (Materials Letters)
巻： 311  ページ： Null  発行年： 2022年 
JST資料番号： E0935A  ISSN： 0167-577X  資料種別： 逐次刊行物 (A)
記事区分： 短報  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： 一次Mnリッチ相に及ぼすAl-Si-Cu-Mn-Ni合金における微量B添加の微細化効果を,OM,SEM,TEMおよびHRTEMによって研究した。微量B(0.02wt%)の添加は,粗大デンドライトから微細な短ロッド状またはブロック状への一次Mnリッチ相の形態を著しく変化させ,そのサイズを著しく減少させた。TEM/HRTEMキャラクタリゼーションは,短ロッド状またはブロック状Al_3MnSi_2相に埋め込まれた微粒子が(V,Ti,Mn)B_2相であることを明らかにした。Al_3MnSi_2相と(V,Ti,Mn)B_2相の間の1つの良好な整合方位関係をE2EMモデル計算により確認し,(V,Ti,Mn)B_2相が凝固中のAl_3MnSi_2相の不均一核形成基板として強い可能性を有することを示した。従って,Al-Si-Cu-Mn-Ni合金におけるBと不純物元素の微量添加は,微細な(V,Ti,Mn)B_2粒子の形成をもたらし,一次Al_3MnSi_2相の核形成を大きく増強し,従って,そのサイズを著しく減少させた。Copyright 2022 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： 核形成 ,  凝固 ,  結晶構造 ,  *合金 ,  *不純物 ,  アルミニウム合金 ,  *耐熱合金 ,  鋳造 ,  *精錬 ,  微粒子 ,  樹枝状結晶 ,  精密化
準シソーラス用語： HRTEM ,  モデル計算 ,  不均一核形成 , 【Automatic Indexing@JST】

著者キーワード (6件)： 鋳造 ,  結晶構造 ,  微細構造 ,  耐熱アルミニウム合金 ,  E2EMモデル ,  精錬効果

分類 (1件)： 変態組織,加工組織  (WB01030N)

タイトルに関連する用語 (10件)： Mn ,  Al ,  Si ,  Cu ,  Ni ,  耐熱合金 ,  不純物 ,  元素 ,  微量添加 ,  精錬