市販純チタンの冷間引抜とミクロ組織および集合組織進展に及ぼすその影響【JST・京大機械翻訳】

Cold Drawing of Commercially Pure Titanium and Its Effect on Microstructure and Texture Evolution

著者 (6件)： Bishoyi B. (Department of Metallurgical & Materials Engineering, NIT Rourkela, Rourkela, India) ,  Vinjamuri R. (Department of Metallurgical & Materials Engineering, NIT Rourkela, Rourkela, India) ,  Sabat R. K. (School of Minerals, Metallurgical and Materials Engineering, IIT Bhubaneswar, Bhubaneswar, India) ,  Patro S. K. (Department of Mechanical Engineering, RIT Berhampur, Berhampur, India) ,  Suwas S. (Department of Materials Engineering, IISc Bangalore, Bangalore, India) ,  Sahoo S. K. (Department of Metallurgical & Materials Engineering, NIT Rourkela, Rourkela, India)
資料名： Metallurgical and Materials Transactions. A. Physical Metallurgy and Materials Science  (Metallurgical and Materials Transactions. A. Physical Metallurgy and Materials Science)
巻： 53  号： 5  ページ： 1845-1858  発行年： 2022年 
JST資料番号： E0265B  ISSN： 1073-5623  CODEN： MTTABN  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： ドイツ (DEU)  言語： 英語 (EN)

抄録/ポイント： 本研究では,市販の純(CP)チタンワイヤの冷間引抜中のミクロ組織と集合組織の進展を調べた。変形の初期粒径,還元割合および歪速度の役割も調べた。引張と圧縮双晶の両方が冷間引抜後の試料で観察され,双晶はより高い還元割合と変形のより高い歪速度で重要でないことが分かった。より大きな粒径の試料は双晶の体積分率が低かった。さらに,双晶はSchmid及び非Schmid型として特性化され,それらは試料中の微細構造発達に類似の影響を及ぼした。冷間引抜後の試料の集合組織は,支配的な基底および角柱配向を有することが観察された。しかし,これらの集合組織成分の強度は,より大きな粒径のサンプルに対して増加した。さらに,変形の初期粒径と歪速度の影響は冷間引抜中の集合組織進展には重要でないことが分かった。Copyright The Minerals, Metals & Materials Society and ASM International 2022 Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： *集合組織 ,  双晶 ,  微細構造 ,  *チタン ,  *金属組織 ,  基底 ,  *冷間引抜 ,  粒径 ,  角柱 ,  引張 ,  歪速度 ,  配向 ,  キャラクタリゼーション ,  体積率
準シソーラス用語： *純チタン , 【Automatic Indexing@JST】

分類 (1件)： 変態組織,加工組織  (WB01030N)

タイトルに関連する用語 (5件)： 純チタン ,  冷間引抜 ,  ミクロ組織 ,  集合組織 ,  進展