Sn-Cu被覆による炭素繊維強化アルミニウムマトリックス複合材料の界面接合と熱伝導率の改善【JST・京大機械翻訳】

Improvement of Interface Bonding and Thermal Conductivity of Carbon-Fiber Reinforced Aluminum Matrix Composites with Sn-Cu Coatings

著者 (17件)： Zhou Qiwen (School of Materials Science and Engineering, Shenyang University of Technology, Shenyang, Liaoning, China) ,  Zhou Qiwen (Key Laboratory of Light Metal Materials and Engineering at Universities of Liaoning Province, Shenyang University of Technology, Shenyang, Liaoning, China) ,  Qu Yingdong (School of Materials Science and Engineering, Shenyang University of Technology, Shenyang, Liaoning, China) ,  Qu Yingdong (Key Laboratory of Light Metal Materials and Engineering at Universities of Liaoning Province, Shenyang University of Technology, Shenyang, Liaoning, China) ,  Li Guanglong (School of Materials Science and Engineering, Shenyang University of Technology, Shenyang, Liaoning, China) ,  Li Guanglong (Key Laboratory of Light Metal Materials and Engineering at Universities of Liaoning Province, Shenyang University of Technology, Shenyang, Liaoning, China) ,  Singh A. (Waikato Centre for Advanced Materials, School of Engineering, University of Waikato, Hamilton, New Zealand) ,  Su Ruiming (School of Materials Science and Engineering, Shenyang University of Technology, Shenyang, Liaoning, China) ,  Su Ruiming (Key Laboratory of Light Metal Materials and Engineering at Universities of Liaoning Province, Shenyang University of Technology, Shenyang, Liaoning, China) ,  Chen Ruirun (School of Materials Science and Engineering, Harbin Institute of Technology, Harbin, Heilongjiang, China) ,  Zhou Shan (School of Materials Science and Engineering, Shenyang University of Technology, Shenyang, Liaoning, China) ,  Zhou Shan (Key Laboratory of Light Metal Materials and Engineering at Universities of Liaoning Province, Shenyang University of Technology, Shenyang, Liaoning, China) ,  Zhao Yu (School of Materials Science and Engineering, Shenyang University of Technology, Shenyang, Liaoning, China) ,  Zhao Yu (Key Laboratory of Light Metal Materials and Engineering at Universities of Liaoning Province, Shenyang University of Technology, Shenyang, Liaoning, China) ,  Yang Fei (Waikato Centre for Advanced Materials, School of Engineering, University of Waikato, Hamilton, New Zealand) ,  Li Rongde (School of Materials Science and Engineering, Shenyang University of Technology, Shenyang, Liaoning, China) ,  Li Rongde (Key Laboratory of Light Metal Materials and Engineering at Universities of Liaoning Province, Shenyang University of Technology, Shenyang, Liaoning, China)
資料名： JOM  (JOM)
巻： 74  号： 5  ページ： 1840-1848  発行年： 2022年 
JST資料番号： C0321A  ISSN： 1047-4838  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： ドイツ (DEU)  言語： 英語 (EN)

抄録/ポイント： 炭素繊維(Cfs)強化アルミニウムマトリックス(Cf/Al)複合材料の界面結合と熱伝導率(TC)は,調製時のCfs表面Cu被覆の容易な酸化と放出により悪化した。本研究では,Sn-Cu被覆を用いてCu被覆を置換し,複合材料の界面とTCを改善した。Sn-Cu被覆は,調製時のCuO生成を防ぎ,Al_4C_3相生成の阻害によって複合材料の界面結合とTCを改善する。1%volSn-Cu被覆炭素繊維を有する複合材料は,炭化物生成が界面で最小化されるので,176W/mKの最大TCを有した。この最大TCは未被覆炭素繊維より25.2%高い。したがって,調製時のCu被覆酸化の防止は,複合材料の界面結合とTCを改善する。Copyright The Minerals, Metals & Materials Society 2022 Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： *界面 ,  酸化 ,  接合 ,  *熱伝導率 ,  複合材料 ,  *銅 ,  炭化物 ,  *被覆 ,  *炭素繊維 ,  結合 ,  酸化第二銅
準シソーラス用語： 三相 , 【Automatic Indexing@JST】

分類 (4件)： 変態組織,加工組織  (WB01030N) ,  炭素とその化合物  (YB02060D) ,  セラミック・磁器の性質  (YC03030G) ,  ろう付  (WC07050C)

タイトルに関連する用語 (9件)： Sn ,  Cu ,  炭素繊維 ,  強化 ,  アルミニウム ,  マトリックス ,  複合材料 ,  界面 ,  熱伝導率