反応性合成により作製した多孔質MoAlBセラミックのミクロサイズ細孔構造に及ぼすアルミニウムの影響【JST・京大機械翻訳】

Effects of aluminum on micro-sized pore structure of porous MoAlB ceramics fabricated via reactive synthesis

著者 (7件)： Yang Junsheng (School of Mechanical Engineering, Wuhan Polytechnic University, Wuhan, 430023, Hubei, China) ,  Wen Yi (School of Mechanical Engineering, Wuhan Polytechnic University, Wuhan, 430023, Hubei, China) ,  Zou Haoran (School of Mechanical Engineering, Wuhan Polytechnic University, Wuhan, 430023, Hubei, China) ,  Fan Yiquan (School of Mechanical Engineering, Wuhan Polytechnic University, Wuhan, 430023, Hubei, China) ,  Zhang Chuo (School of Mechanical Engineering, Wuhan Polytechnic University, Wuhan, 430023, Hubei, China) ,  Xiong Lieqiang (School of Mechanical Engineering, Wuhan Polytechnic University, Wuhan, 430023, Hubei, China) ,  Zhang Kaisong (School of Mechanical Engineering, Wuhan Polytechnic University, Wuhan, 430023, Hubei, China)
資料名： Ceramics International  (Ceramics International)
巻： 48  号： 10  ページ： 14151-14155  発行年： 2022年 
JST資料番号： H0705A  ISSN： 0272-8842  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： Mo,Al,およびB粉末をモル比1/n/1(n,1.4~1.9,0.1増分)で用いて,多孔質MoAlBセラミックを活性化反応技術で完全に合成した。相変態,体積膨張,微細構造および細孔構造パラメータ(細孔径,多孔性および透過率を含む)に及ぼすアルミニウム含有量の影響を,系統的に調査した。1.4から1.9へのAl含有量の増加とともに,開放多孔性は,最初にゆっくり増加し,次に,成長速度の増加の傾向を明らかにした。一方,体積膨張,細孔径および透過性は,開放多孔性と類似の傾向を示した。これらの細孔構造パラメータ変化進展の理由を徹底的に調査した。細孔形成メカニズムも調べた。Copyright 2022 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： *セラミック ,  微細構造 ,  粉体 ,  *アルミニウム ,  多孔性 ,  位相 ,  透過率 ,  空隙率 ,  細孔径 ,  細孔 ,  構造パラメータ ,  成長速度 ,  細孔構造 ,  モル比
準シソーラス用語： 体積膨張 , 【Automatic Indexing@JST】

著者キーワード (4件)： セラミック ,  位相構成 ,  空隙率 ,  細孔形成メカニズム