石膏から調製したチタン酸カルシウムの構造的および光学的性質【JST・京大機械翻訳】

Structural and Optical Properties of Calcium Titanate Prepared from Gypsum

著者 (8件)： Mostafa Massaud (Physics Department, College of Science, Jouf University, Sakaka, Saudi Arabia) ,  Mostafa Massaud (Laser Technology & Environment Laboratory, Physics Department, Faculty of Science, South Valley University, Qena 83523, Egypt) ,  Alrowaili Z. A. (Physics Department, College of Science, Jouf University, Sakaka, Saudi Arabia) ,  Al Shehri M.M. (Physics Department, College of Science, Jouf University, Sakaka, Saudi Arabia) ,  Mobarak M. (Physics Department, College of Science, Jouf University, Sakaka, Saudi Arabia) ,  Mobarak M. (Physics Department, Faculty of Science, South Valley University, Qena 83523, Egypt) ,  Abbas Ahmed M. (Biology Department, College of Science, King Khalid University, Abha 61413, Saudi Arabia) ,  Abbas Ahmed M. (Department of Botany and Microbiology, Faculty of Science, South Valley University, Qena 83523, Egypt)
資料名： Journal of Nanotechnology (Web)  (Journal of Nanotechnology (Web))
巻： 2022  ページ： Null  発行年： 2022年 
JST資料番号： U7777A  ISSN： 1687-9503  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： セラミック材料は,様々なヒト健康関連用途においてかなりの時間に使用されている。セラミック材料の重要な応用の一つはエレクトロニクスである。本研究はチタン酸カルシウム(CaTiO_3)に焦点を当てた。CaTiO_3は焼結により典型的に生成した。石膏粒子を用いて水酸化カルシウムを形成し,次に二酸化チタンと結合してルチル結晶を形成した。その後,焼成は900°C,1000°C,1100°Cで2時間行った。X線回折を用いてCaTiO_3相の進展を追跡した。走査電子顕微鏡を用いて,異なる調製段階の形態を特性化した。焼成温度が900°Cから1000°Cに上昇すると,CaTiO_3の結晶サイズは35nmから45nmに増加した。さらに,900°Cと1000°Cでのか焼後に得られたCaTiO_3粉末のエネルギーギャップは,それぞれ5.32eVと5.43eVであり,それらの粒径は,それぞれ150-200nmと200-300nmであった。Copyright 2022 Massaud Mostafa et al. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： X線回折 ,  エネルギーギャップ ,  焼結 ,  セラミック ,  走査電子顕微鏡 ,  粉体 ,  *石膏 ,  水酸化カルシウム ,  X線回折分析 ,  酸化チタン ,  ヒト ,  ルチル ,  か焼 ,  電子技術 ,  *チタン酸カルシウム
準シソーラス用語： 二酸化チタン ,  焼成温度 , 【Automatic Indexing@JST】

分類 (2件)： 塩  (CD01050V) ,  セラミック・陶磁器の製造  (YC03020V)

引用文献 (22件)：

• R. Acharya, K. Parida, "A review on TiO₂/g-C₃N₄ visible-light- responsive photocatalysts for sustainable energy generation and environmental remediation," Journal of Environmental Chemical Engineering, vol. 8, no. 4, 2020.
• P. A. Owusu, S. Asumadu-Sarkodie, "A review of renewable energy sources, sustainability issues and climate change mitigation," Cogent Engineering, vol. 3, no. 1, 2016.
• K. Qi, B. Cheng, J. Yu, W. Ho, "A review on TiO₂ -based Z-scheme photocatalysts," Chinese Journal of Catalysis, vol. 38, no. 12, pp. 1936-1955, 2017.
• L. Finegold, J. L. Cude, "Biological sciences: one and two-dimensional structure of alpha-helix and beta-sheet forms of poly(L-alanine) shown by specific heat measurements at low temperatures (1.5-20 K)," Nature, vol. 238, no. 5358, pp. 38-40, 1972.
• H. Wang, L. Zhang, Z. Chen, J. Hu, S. Li, Z. Wang, J. Liu, X. Wang, "Semiconductor heterojunction photocatalysts: design, construction, and photocatalytic performances," Chemical Society Reviews, vol. 43, no. 15, pp. 5234-5244, 2014.

タイトルに関連する用語 (4件)： 石膏 ,  調製 ,  チタン酸カルシウム ,  光学的性質