SmドープGd_2Zr_2O_7透明セラミックの作製と発光特性【JST・京大機械翻訳】

Fabrication and luminescent properties of Sm-doped Gd₂Zr₂O₇ transparent ceramics

著者 (5件)： Yu Lei (School of Materials Engineering, Changshu Institute of Technology, Changshu, 215500, China) ,  Zhang Kuibao (School of Materials Engineering, Changshu Institute of Technology, Changshu, 215500, China) ,  Zhang Kuibao (State Key Laboratory of Environment-friendly Energy Materials, Southwest University of Science and Technology, Mianyang, Sichuan, 621010, China) ,  Li Weiwei (State Key Laboratory of Environment-friendly Energy Materials, Southwest University of Science and Technology, Mianyang, Sichuan, 621010, China) ,  Luo Baozhu (State Key Laboratory of Environment-friendly Energy Materials, Southwest University of Science and Technology, Mianyang, Sichuan, 621010, China)
資料名： Journal of Luminescence  (Journal of Luminescence)
巻： 243  ページ： Null  発行年： 2022年 
JST資料番号： D0731A  ISSN： 0022-2313  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： 本研究では,SmドープGd_2Zr_2O_7透明セラミックを,燃焼合成ナノ粉末を用いた高温真空焼結により調製した。X線回折,固体紫外吸収分光光度計および蛍光分光計を用いて,調製したままの試料の構造変化および光ルミネセンス特性を調べた。SmドープGd_2Zr_2O_7ナノ粉末は欠陥蛍石構造であり,高温焼結後にパイロクロア構造に変態する。3%Smドープ試料は,1000nmの波長で74.7%の高いインライン透過率を示した。404nmで励起し,615nmで検出したすべての試料の蛍光寿命はミリ秒スケールであり,Smドーピング濃度が10%に達すると濃度消光が生じた。Copyright 2022 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： X線回折 ,  蛍光 ,  高温 ,  焼結 ,  *セラミック ,  光ルミネセンス ,  *サマリウム ,  波長 ,  *ドーピング ,  透過率 ,  分光計 ,  蛍光寿命 ,  燃焼合成
準シソーラス用語： パイロクロア ,  ナノ粉末 , 【Automatic Indexing@JST】

著者キーワード (5件)： 透明セラミック ,  Gd_2Zr_2O_7 ,  真空焼結 ,  透過率 ,  蛍光