表面酸化後のWTe_2におけるバンド曲げの観測【JST・京大機械翻訳】

Observation of band bending in WTe₂ after surface oxidation

著者 (17件)： Chen Aixi (Vacuum Interconnected Nanotech Workstation (Nano-X), Suzhou Institute of Nano-Tech and Nano-Bionics (SINANO), Chinese Academy of Sciences (CAS), Suzhou 215123, China) ,  Li Huifang (Vacuum Interconnected Nanotech Workstation (Nano-X), Suzhou Institute of Nano-Tech and Nano-Bionics (SINANO), Chinese Academy of Sciences (CAS), Suzhou 215123, China) ,  Huang Rong (Vacuum Interconnected Nanotech Workstation (Nano-X), Suzhou Institute of Nano-Tech and Nano-Bionics (SINANO), Chinese Academy of Sciences (CAS), Suzhou 215123, China) ,  Zhao Yanfei (Vacuum Interconnected Nanotech Workstation (Nano-X), Suzhou Institute of Nano-Tech and Nano-Bionics (SINANO), Chinese Academy of Sciences (CAS), Suzhou 215123, China) ,  Liu Tong (Vacuum Interconnected Nanotech Workstation (Nano-X), Suzhou Institute of Nano-Tech and Nano-Bionics (SINANO), Chinese Academy of Sciences (CAS), Suzhou 215123, China) ,  Li Zhiyun (Vacuum Interconnected Nanotech Workstation (Nano-X), Suzhou Institute of Nano-Tech and Nano-Bionics (SINANO), Chinese Academy of Sciences (CAS), Suzhou 215123, China) ,  Wang Li (Vacuum Interconnected Nanotech Workstation (Nano-X), Suzhou Institute of Nano-Tech and Nano-Bionics (SINANO), Chinese Academy of Sciences (CAS), Suzhou 215123, China) ,  Chen Feiyu (Vacuum Interconnected Nanotech Workstation (Nano-X), Suzhou Institute of Nano-Tech and Nano-Bionics (SINANO), Chinese Academy of Sciences (CAS), Suzhou 215123, China) ,  Ren Wei (Vacuum Interconnected Nanotech Workstation (Nano-X), Suzhou Institute of Nano-Tech and Nano-Bionics (SINANO), Chinese Academy of Sciences (CAS), Suzhou 215123, China) ,  Ren Wei (School of Nano-Tech and Nano-Bionics, University of Science and Technology of China, Hefei 230026, China) ,  Lu Shuai (Vacuum Interconnected Nanotech Workstation (Nano-X), Suzhou Institute of Nano-Tech and Nano-Bionics (SINANO), Chinese Academy of Sciences (CAS), Suzhou 215123, China) ,  Yang Bingjie (Vacuum Interconnected Nanotech Workstation (Nano-X), Suzhou Institute of Nano-Tech and Nano-Bionics (SINANO), Chinese Academy of Sciences (CAS), Suzhou 215123, China) ,  Huang Zengli (Vacuum Interconnected Nanotech Workstation (Nano-X), Suzhou Institute of Nano-Tech and Nano-Bionics (SINANO), Chinese Academy of Sciences (CAS), Suzhou 215123, China) ,  Ding Sunan (Vacuum Interconnected Nanotech Workstation (Nano-X), Suzhou Institute of Nano-Tech and Nano-Bionics (SINANO), Chinese Academy of Sciences (CAS), Suzhou 215123, China) ,  Ding Sunan (School of Nano-Tech and Nano-Bionics, University of Science and Technology of China, Hefei 230026, China) ,  Li Fang-Sen (Vacuum Interconnected Nanotech Workstation (Nano-X), Suzhou Institute of Nano-Tech and Nano-Bionics (SINANO), Chinese Academy of Sciences (CAS), Suzhou 215123, China) ,  Li Fang-Sen (School of Nano-Tech and Nano-Bionics, University of Science and Technology of China, Hefei 230026, China)
資料名： Surface Science  (Surface Science)
巻： 716  ページ： Null  発行年： 2022年 
JST資料番号： C0129B  ISSN： 0039-6028  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： 最近,半金属特性を有するWTe_2関連デバイスにおける自然面外電気分極と強誘電スイッチングの観測が,かなりの注目を集めている。WTe_2の極性構造は極めて重要であるが,詳細な表面分析に値する物理的起源についてはまだコンセンサスがない。ここでは,角度依存X線光電子分光法(ADXPS)を用いて,わずかに表面酸化後,WTe_2で明らかな下方バンド曲がりを観測し,これは新たに切断されたWTe_2では観察できなかった。そして,それは完全酸化の後消えて,バンド曲げと表面酸化の間の強い相関を示した。本研究は,WTe_2における表面酸化と結果としてのバンド曲がりが,強誘電体のようなWTe_2関連デバイスで考慮されるべきであることを示唆する。Copyright 2022 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： 強誘電体 ,  極性 ,  *酸化 ,  表面分析 ,  誘電分極 ,  角度依存性 ,  金属性 ,  X線光電子分光法
準シソーラス用語： *表面酸化 ,  完全酸化 ,  バンド曲がり ,  強誘電スイッチング , 【Automatic Indexing@JST】

著者キーワード (4件)： WTe_2 ,  バンド曲げ ,  酸化 ,  角度依存XPS

分類 (5件)： 表面の電子構造  (BM02080J) ,  不純物・欠陥の電子構造  (BM02100I) ,  電子分光スペクトル  (BM09060K) ,  吸着の電子論  (CB12042Y) ,  酸化物薄膜  (BK14050P)

タイトルに関連する用語 (4件)： 表面酸化 ,  バンド ,  曲げ ,  観測