レーザ粉末層溶融付加製造による高エントロピー合金/金属ガラスのバイメタル印刷【JST・京大機械翻訳】

Bimetal printing of high entropy alloy/metallic glass by laser powder bed fusion additive manufacturing

著者 (15件)： Wang Hao (Guangdong Provincial Key Laboratory of Micro/Nano Optomechatronics Engineering, College of Mechatronics and Control Engineering, Shenzhen University, Shenzhen, 518060, China) ,  Chen Junquan (Guangdong Provincial Key Laboratory of Micro/Nano Optomechatronics Engineering, College of Mechatronics and Control Engineering, Shenzhen University, Shenzhen, 518060, China) ,  Chen Junquan (State Key Laboratory of Materials Processing and Die & Mould Technology, Huazhong University of Science and Technology, Wuhan, 430074, China) ,  Chen Junquan (Department of Materials Science and Engineering, Southern University of Science and Technology, Shenzhen, 518055, China) ,  Luo Hailu (Guangdong Provincial Key Laboratory of Micro/Nano Optomechatronics Engineering, College of Mechatronics and Control Engineering, Shenzhen University, Shenzhen, 518060, China) ,  Luo Hailu (State Key Laboratory of Materials Processing and Die & Mould Technology, Huazhong University of Science and Technology, Wuhan, 430074, China) ,  Luo Hailu (Department of Materials Science and Engineering, Southern University of Science and Technology, Shenzhen, 518055, China) ,  Wang Di (Department of Mechanical and Automotive Engineering, South China University of Technology, Guangzhou, China) ,  Song Changhui (Department of Mechanical and Automotive Engineering, South China University of Technology, Guangzhou, China) ,  Yao Xiyu (State Key Laboratory of Materials Processing and Die & Mould Technology, Huazhong University of Science and Technology, Wuhan, 430074, China) ,  Yao Xiyu (Department of Materials Science and Engineering, Southern University of Science and Technology, Shenzhen, 518055, China) ,  Chen Peng (State Key Laboratory of Materials Processing and Die & Mould Technology, Huazhong University of Science and Technology, Wuhan, 430074, China) ,  Chen Peng (Department of Materials Science and Engineering, Southern University of Science and Technology, Shenzhen, 518055, China) ,  Yan Ming (State Key Laboratory of Materials Processing and Die & Mould Technology, Huazhong University of Science and Technology, Wuhan, 430074, China) ,  Yan Ming (Department of Materials Science and Engineering, Southern University of Science and Technology, Shenzhen, 518055, China)
資料名： Intermetallics  (Intermetallics)
巻： 141  ページ： Null  発行年： 2022年 
JST資料番号： W0672A  ISSN： 0966-9795  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： 独特の微細構造と性質を有する金属材料として,高エントロピー合金(HEAs)と金属ガラス(MG)は,それぞれの利点を有する。本研究では,レーザ粉末層(LPBF)添加物製造(AM)を用いて,典型的な五元HEA(CoCrFeMnNi)とFeベースMGの間のバイメタル印刷を実現し,両材料の特性を継承した。その結果,両合金から成るバルク材料は,印刷したMGと,印刷したHEAに起因する強度と延性の良好な組合せから,著しく高い硬度(~251HVから~1210HVまで)と耐食性(約0.967mm/年から~0.765mm/年)を示した。透過電子顕微鏡と電子後方散乱回折を含む分析手段を用いて,微細構造,特に良好なインターロッキング接合を形成するのに不可欠なHEA/MG界面を詳細に説明した。本研究は,特にHEAsとMGを含む先進材料の開発におけるLPBFバイメタル印刷の能力を実証した。Copyright 2022 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： 延性 ,  界面 ,  *合金 ,  *印刷 ,  鉄 ,  金属材料 ,  *バイメタル ,  耐食性 ,  *粉体層 ,  透過型電子顕微鏡 ,  レーザ融解 ,  *金属ガラス ,  *付加製造
準シソーラス用語： EBSD ,  *高エントロピー合金 , 【Automatic Indexing@JST】

著者キーワード (5件)： 選択的レーザ融解(SLM) ,  レーザ粉体層核融合(LPBF) ,  バイメタル印刷 ,  高エントロピー合金(HEA) ,  金属ガラス(MG)

分類 (2件)： 変態組織,加工組織  (WB01030N) ,  機械的性質  (WB02030U)

タイトルに関連する用語 (7件)： レーザ ,  粉末層 ,  溶融 ,  付加製造 ,  高エントロピー合金 ,  金属ガラス ,  バイメタル