CrMoTaTi耐熱高エントロピー合金の高温酸化挙動に及ぼすYの影響【JST・京大機械翻訳】

Effect of Y on the high-temperature oxidation behavior of CrMoTaTi refractory high entropy alloy

著者 (7件)： Du Yuhang (School of Materials and Energy, Southwest University, Chongqing 400715, China) ,  Ding Deyu (School of Materials and Energy, Southwest University, Chongqing 400715, China) ,  Lai Limin (School of Materials and Energy, Southwest University, Chongqing 400715, China) ,  Xiao Siming (School of Materials and Energy, Southwest University, Chongqing 400715, China) ,  Guo Ning (School of Materials and Energy, Southwest University, Chongqing 400715, China) ,  Song Bo (School of Materials and Energy, Southwest University, Chongqing 400715, China) ,  Guo Shengfeng (School of Materials and Energy, Southwest University, Chongqing 400715, China)
資料名： International Journal of Refractory Metals & Hard Materials  (International Journal of Refractory Metals & Hard Materials)
巻： 103  ページ： Null  発行年： 2022年 
JST資料番号： H0059B  ISSN： 0263-4368  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： 耐火高エントロピー合金(RHEAs)は通常,高温で良好な機械的性質を示した。残念なことに,非常に貧弱な高温耐酸化性は,それらの実用化空間を大きく制限した。本研究では,CrMoTaTi RHEAの高温耐酸化性に及ぼす反応性元素(RE)Yの影響を系統的に調べた。Yの添加はCrMoTaTi RHEAの高温酸化抵抗を著しく改善できることが分かった。Y含有RHEAsに対して,それらは合金表面上のCr_2O_3の生成に必要なCrの臨界濃度を大きく減少させ,それはTa_2O_5と反応したCr_2O_3の急速な形成に寄与し,比較的緻密で連続的な保護層を有するCrTaO_4の生成をもたらした。Y含有RHEAsは,合金を1000°Cで100時間酸化した場合でも良好な耐酸化性を示した。本研究では,反応性元素の正の役割と,RHEAsの高温酸化抵抗を改善する新しい洞察を提案した。Copyright 2022 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： 機械的性質 ,  *高温 ,  *合金 ,  *酸化 ,  *クロム ,  *高温酸化 ,  耐酸化性 ,  反応 ,  耐火性
準シソーラス用語： 臨界濃度 ,  選択酸化 ,  保護層 ,  *高エントロピー合金 ,  *酸化挙動 ,  高温耐酸化性 , 【Automatic Indexing@JST】