(HfMoTiWZr)C高エントロピー炭化物セラミックの合成とキャラクタリゼーション【JST・京大機械翻訳】

Synthesis and characterization of (HfMoTiWZr)C high entropy carbide ceramics

著者 (11件)： Kavak Sina (Istanbul Technical University, Faculty of Chemical and Metallurgical Engineering, Department of Metallurgical and Materials Engineering, Particulate Materials Laboratories (PML), 34469, Maslak, Istanbul, Turkey) ,  Bayrak Kuebra Guercan (Eskisehir Technical University, Faculty of Engineering, Department of Materials Science and Engineering, Iki Eyluel Campus, 26555, Eskisehir, Turkey) ,  Bellek Mustafa (Istanbul Technical University, Faculty of Chemical and Metallurgical Engineering, Department of Metallurgical and Materials Engineering, Particulate Materials Laboratories (PML), 34469, Maslak, Istanbul, Turkey) ,  Bellek Mustafa (ASELSAN Inc., Teknopark Istanbul, 34906, Istanbul, Turkey) ,  Mertdinc Siddika (Istanbul Technical University, Faculty of Chemical and Metallurgical Engineering, Department of Metallurgical and Materials Engineering, Particulate Materials Laboratories (PML), 34469, Maslak, Istanbul, Turkey) ,  Muhaffel Faiz (Istanbul Technical University, Faculty of Chemical and Metallurgical Engineering, Department of Metallurgical and Materials Engineering, 34469, Maslak, Istanbul, Turkey) ,  Gokce Hasan (Istanbul Technical University, Prof. Dr. Adnan Tekin Materials Science and Production Technologies Applied Research Center (ATARC), 34469, Maslak, Istanbul, Turkey) ,  Ayas Erhan (Eskisehir Technical University, Faculty of Engineering, Department of Materials Science and Engineering, Iki Eyluel Campus, 26555, Eskisehir, Turkey) ,  Derin Bora (Istanbul Technical University, Faculty of Chemical and Metallurgical Engineering, Department of Metallurgical and Materials Engineering, 34469, Maslak, Istanbul, Turkey) ,  OEvecoglu M. Luetfi (Istanbul Technical University, Faculty of Chemical and Metallurgical Engineering, Department of Metallurgical and Materials Engineering, Particulate Materials Laboratories (PML), 34469, Maslak, Istanbul, Turkey) ,  Agaogullari Duygu (Istanbul Technical University, Faculty of Chemical and Metallurgical Engineering, Department of Metallurgical and Materials Engineering, Particulate Materials Laboratories (PML), 34469, Maslak, Istanbul, Turkey)
資料名： Ceramics International  (Ceramics International)
巻： 48  号： 6  ページ： 7695-7705  発行年： 2022年 
JST資料番号： H0705A  ISSN： 0272-8842  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： (HfMoTiWZr)C高エントロピー炭化物(HEC)を,高エネルギーボールミル処理(HEBM)および放電プラズマ焼結(SPS)により,周期的テーブルのIVB(Hf,Ti,Zr)およびVIB(Mo,W)族金属の市販炭化物粉末から調製した。炭化金属粉末(HfC,TiC,ZrC,Mo_2CおよびWC)を,振動ボールミルで3時間HEBM’dで,次に,種々の温度(1800,1900,2000および2100°C)でSPS’dとした。HEBM’d粉末とSPS’dセラミックを,X線回折計(XRD),走査電子顕微鏡/エネルギー分散分光計(SEM/EDS),粒径分析器,およびピクノメータを用いて,組成,密度,および微細構造において特性評価した。また,微小硬さと滑り摩耗試験をSPS’dセラミックで行った。実施した特性評価に基づいて,単相FCC構造をすべての焼結温度で観察し,高いエントロピー炭化物セラミックを示し,それらはすべて高い硬度と耐摩耗性値を有する。Copyright 2022 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： X線回折 ,  *エントロピー ,  焼結 ,  *セラミック ,  走査電子顕微鏡 ,  微小硬さ ,  粉体 ,  ボールミル ,  *炭化物 ,  比重計 ,  金属粉末 ,  X線回折分析 ,  *炭化 ,  単相 ,  滑り摩耗 ,  放電プラズマ焼結

著者キーワード (5件)： フライス加工 ,  焼結 ,  微細構造-最終 ,  機械的性質 ,  高エントロピー炭化物

分類 (2件)： セラミック・磁器の性質  (YC03030G) ,  セラミック・陶磁器の製造  (YC03020V)

タイトルに関連する用語 (4件)： エントロピー ,  炭化物 ,  セラミック ,  キャラクタリゼーション