アニーリング下のTiZrNi被覆の構造と機械的性質の評価【JST・京大機械翻訳】

Evaluation of structure and mechanical properties of TiZrNi coatings under annealing

著者 (8件)： Penkov Oleksiy V. (ZJU-UIUC Institute, International Campus, Zhejiang University, Haining 314400, China) ,  Penkov Oleksiy V. (Department of Mechanical Science and Engineering, University of Illinois at Urbana-Champaign, Urbana, IL 61801, USA) ,  Kopylets Igor A. (National Technical University ”KhPI, Kharkiv 61002, Ukraine) ,  Khadem M. (Department of Mechanical Engineering, Yonsei University, Seoul 03722, South Korea) ,  Kondratenko Valeriy V. (National Technical University ”KhPI, Kharkiv 61002, Ukraine) ,  Malykhin Sergiy V. (National Technical University ”KhPI, Kharkiv 61002, Ukraine) ,  Surovitskiy Sergiy V. (National Technical University ”KhPI, Kharkiv 61002, Ukraine) ,  Fedchenko Anna V. (National Technical University ”KhPI, Kharkiv 61002, Ukraine)
資料名： Thin Solid Films  (Thin Solid Films)
巻： 748  ページ： Null  発行年： 2022年 
JST資料番号： B0899A  ISSN： 0040-6090  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： Ti41Zr39Ni20皮膜の構造と機械的性質に及ぼすアニーリング温度の影響を調べた。コーティングをマグネトロンスパッタリングによりステンレス鋼基板上に堆積し,次に200から850°Cの温度において真空中でアニールした。焼鈍中の構造と機械的性質の評価を,断面透過電子顕微鏡,X線回折分析,および超ナノインデンテーションを用いて行った。さらに,機械的耐久性を往復滑り試験により評価した。コーティングの機械的特性と構造相特性の間の関係を確立した。結果は,2/1近似相の機械的特性が,おそらく2/1近似相の原子結晶構造の特殊性のため,準結晶相のものより良いことを示唆した。さらに,600°Cで焼なました皮膜では,不均一相転移に起因する層状構造の形成が観察された。最上層のナノ結晶構造と2/1近似相の高濃度は,最高の硬度(25GPa)と硬度/弾性比(0.14)をもたらした。Copyright 2022 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： 結晶構造 ,  *焼なまし ,  相転移 ,  ステンレス鋼 ,  弾性 ,  *被覆 ,  X線回折分析 ,  近似法 ,  層状組織 ,  皮膜 ,  準結晶
準シソーラス用語： アニーリング温度 ,  往復滑り , 【Automatic Indexing@JST】

著者キーワード (5件)： TiZrNi ,  準結晶 ,  塗料 ,  ナノ構造 ,  機械的性質