酸素発生反応のための強力な電極触媒としての種々のアニオンを有するFe/Ni二金属有機骨格【JST・京大機械翻訳】

Fe/Ni bimetallic organic framework with varying anions as robust electrocatalyst for oxygen evolution reaction

著者 (4件)： Wang Na (Hebei Key Laboratory of Applied Chemistry, College of Environmental and Chemical Engineering, Yanshan University, Qinhuangdao, Hebei, 066004, China) ,  Qi Xinjing (Hebei Key Laboratory of Applied Chemistry, College of Environmental and Chemical Engineering, Yanshan University, Qinhuangdao, Hebei, 066004, China) ,  Yu Jinchang (Hebei Key Laboratory of Applied Chemistry, College of Environmental and Chemical Engineering, Yanshan University, Qinhuangdao, Hebei, 066004, China) ,  Chen Yan (Hebei Key Laboratory of Applied Chemistry, College of Environmental and Chemical Engineering, Yanshan University, Qinhuangdao, Hebei, 066004, China)
資料名： International Journal of Hydrogen Energy  (International Journal of Hydrogen Energy)
巻： 47  号： 15  ページ： 9295-9300  発行年： 2022年 
JST資料番号： B0192B  ISSN： 0360-3199  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： 金属-有機骨格(MOF)の性能は,添加したアニオンが異なるとき,影響を受けるであろう。ここでは,二金属FeNi-MOFを,基板としてニッケル発泡体を用いた水熱法により合成し,MOFの材料性能に及ぼす4つのアニオン(Cl-,NO_3-,CH_3COO-,SO_42-)の影響を調べた。100mA・cm-2で247mVの過電位で塩化物イオンを添加すると,MOFを調製した。一方,100mAcm-2で12時間の安定性試験は,高い電気化学的安定性を示す明らかな変化を示さなかった。分析は,塩化物イオンを添加したとき調製したMOFの優れた性能が,低い電荷移動抵抗,増加した活性面積,より活発なサイトへの曝露に起因することを示した。本研究は,前駆体のアニオンを調整することによって,超高性能OER触媒の容易な合成にいくつかの光を投げかけるであろう。Copyright 2022 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： 安定性 ,  水熱合成 ,  *ニッケル ,  *触媒 ,  過電圧 ,  試験 ,  *電極触媒 ,  *アニオン ,  電気化学 ,  前駆体 ,  触媒調製
準シソーラス用語： 塩化物イオン ,  発泡体 ,  化学的安定性 ,  電荷移動抵抗 ,  *酸素発生反応 ,  安定性試験 ,  *MOF【配位高分子】 , 【Automatic Indexing@JST】