効率的な経路による綿からの異なる結晶構造を有するセルロースナノ結晶に関する包括的研究【JST・京大機械翻訳】

A comprehensive investigation on cellulose nanocrystals with different crystal structures from cotton via an efficient route

著者 (8件)： Huang Chengling (Key Laboratory of Advanced Textile Materials and Manufacturing Technology, Ministry of Education, Zhejiang Provincial Key Laboratory of Fiber Materials and Manufacturing Technology, Zhejiang Sci-Tech University, Xiasha Higher Education Park Avenue 2 No.928, Hangzhou 310018, China) ,  Yu Houyong (Key Laboratory of Advanced Textile Materials and Manufacturing Technology, Ministry of Education, Zhejiang Provincial Key Laboratory of Fiber Materials and Manufacturing Technology, Zhejiang Sci-Tech University, Xiasha Higher Education Park Avenue 2 No.928, Hangzhou 310018, China) ,  Abdalkarim Somia Yassin Hussain (Key Laboratory of Advanced Textile Materials and Manufacturing Technology, Ministry of Education, Zhejiang Provincial Key Laboratory of Fiber Materials and Manufacturing Technology, Zhejiang Sci-Tech University, Xiasha Higher Education Park Avenue 2 No.928, Hangzhou 310018, China) ,  Li Yingzhan (Key Laboratory of Advanced Textile Materials and Manufacturing Technology, Ministry of Education, Zhejiang Provincial Key Laboratory of Fiber Materials and Manufacturing Technology, Zhejiang Sci-Tech University, Xiasha Higher Education Park Avenue 2 No.928, Hangzhou 310018, China) ,  Chen Xiang (Key Laboratory of Advanced Textile Materials and Manufacturing Technology, Ministry of Education, Zhejiang Provincial Key Laboratory of Fiber Materials and Manufacturing Technology, Zhejiang Sci-Tech University, Xiasha Higher Education Park Avenue 2 No.928, Hangzhou 310018, China) ,  Yang Xiaogang (Key Laboratory of Advanced Textile Materials and Manufacturing Technology, Ministry of Education, Zhejiang Provincial Key Laboratory of Fiber Materials and Manufacturing Technology, Zhejiang Sci-Tech University, Xiasha Higher Education Park Avenue 2 No.928, Hangzhou 310018, China) ,  Zhou Ying (Key Laboratory of Advanced Textile Materials and Manufacturing Technology, Ministry of Education, Zhejiang Provincial Key Laboratory of Fiber Materials and Manufacturing Technology, Zhejiang Sci-Tech University, Xiasha Higher Education Park Avenue 2 No.928, Hangzhou 310018, China) ,  Zhang Lianyang (Key Laboratory of Clean Dyeing and Finishing Technology of Zhejiang Province, Shaoxing University, Shaoxing 312000, China)
資料名： Carbohydrate Polymers  (Carbohydrate Polymers)
巻： 276  ページ： Null  発行年： 2022年 
JST資料番号： E0961A  ISSN： 0144-8617  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： セルロースナノ材料の結晶構造は,それらのモルフォロジーと応用において重要な役割を果たすが,高い熱安定性を有するセルロースナノ結晶の様々な結晶異形体を調製する系統的研究がまだ不足している。ここでは,綿からセルロースの種々の結晶形態を設計するために,効率的な合成ルートを提示した。そして,異なる結晶構造を有するセルロースナノ結晶(CNC-I,CNC-III_II,CNC-IV_II)を,得られたセルロースの過酸化水素加水分解によって調製した。全体として,針様CNC-I(長さ180±25nm,直径12±2nm),球状CNC-II(直径101±12nm),および球状CNC-III_II(直径22±3nm)およびCNC-IV_II(直径21±2nm)は全て顕著な分散性および熱安定性(T_max>357°C)を示した。本研究は,同じ原材料(綿)から高い熱安定性を有するCNCの様々な結晶形態に対する簡単で低コストの合成ルートを提供する。Copyright 2022 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： *結晶構造 ,  *セルロース ,  加水分解 ,  熱安定性 ,  過酸化水素 ,  分散度 ,  結晶形態 ,  モルフォロジー ,  ナノ材料
準シソーラス用語： *セルロースナノ結晶 , 【Automatic Indexing@JST】

著者キーワード (4件)： セルロースナノ結晶 ,  多形 ,  形態 ,  熱安定性

分類 (1件)： 多糖類  (CF10054P)

タイトルに関連する用語 (5件)： 経路 ,  綿 ,  結晶構造 ,  セルロースナノ結晶 ,  研究