天然再生可能クリシンおよびフルフリルアミンからのバイオベンゾオキサジン樹脂の熱潜在性および低温重合【JST・京大機械翻訳】

Thermal latent and Low-Temperature polymerization of a Bio-Benzoxazine resin from natural renewable chrysin and furfurylamine

著者 (4件)： Zhao Wenqian (Research School of Polymeric Materials, School of Materials Science and Engineering, Jiangsu University, Zhenjiang, Jiangsu 212013, PR China) ,  Hao Boran (Research School of Polymeric Materials, School of Materials Science and Engineering, Jiangsu University, Zhenjiang, Jiangsu 212013, PR China) ,  Lu Yin (Research School of Polymeric Materials, School of Materials Science and Engineering, Jiangsu University, Zhenjiang, Jiangsu 212013, PR China) ,  Zhang Kan (Research School of Polymeric Materials, School of Materials Science and Engineering, Jiangsu University, Zhenjiang, Jiangsu 212013, PR China)
資料名： European Polymer Journal  (European Polymer Journal)
巻： 166  ページ： Null  発行年： 2022年 
JST資料番号： B0690A  ISSN： 0014-3057  CODEN： EUPJA  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： 再生可能なクリシンとフルフリルアミンから低温重合特性を示す新規バイオベンゾオキサジン熱硬化性樹脂(CHR-fa)を合成した。CHR-faの構造をFourier変換赤外(FT-IR)と核磁気共鳴(NMR)分光法と元素分析によって確認した。CHR-fa中のフェノール性水酸基とカルボニル基間の分子内水素結合を,その熱潜在触媒重合挙動を研究するための本質的な構造特性として同定した。CHR-faから誘導したポリベンゾオキサジン被覆は,水接触角97.1°の高い疎水性を示した。さらに,このバイオベースモノベンゾオキサジンに基づくポリベンゾオキサジンは,366°Cの10wt%損失温度,48%の高いチャー収率(800°C,N_2),および43.3J/(gK)の非常に低い熱放出容量を有する高い熱安定性を示した。本研究で開発した複合利点は,高性能材料を製造するための熱硬化性樹脂マトリックスとしてのバイオベースモノベンゾオキサジンの可能性を強調する。Copyright 2022 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： Fourier変換 ,  NMR【磁気共鳴】 ,  赤外線 ,  *低温 ,  熱放射 ,  フェノール樹脂 ,  被覆 ,  元素分析 ,  *重合 ,  疎水性 ,  チャー ,  カルボニル基 ,  構造特性 ,  分子内水素結合
準シソーラス用語： ポリベンゾオキサジン ,  水接触角 , 【Automatic Indexing@JST】

著者キーワード (5件)： ベンゾオキサジン ,  クリシン ,  バイオベース ,  熱潜在性重合 ,  高い熱安定性