粉末溶融紡糸リボンを用いた押出MnAl-C-Ni磁石における非再結晶領域の除去【JST・京大機械翻訳】

Elimination of the non-recrystallised regions in the extruded MnAl-C-Ni magnet using pulverised melt-spun ribbons

著者 (7件)： Feng Le (Leibniz IFW Dresden, Helmholtzstr. 20, 01069 Dresden, Germany) ,  Feng Le (TU Dresden, Institute of Materials Science, 01062 Dresden, Germany) ,  Freudenberger Jens (Leibniz IFW Dresden, Helmholtzstr. 20, 01069 Dresden, Germany) ,  Freudenberger Jens (TU Bergakademie Freiberg, Institute of Materials Science, Gustav-Zeuner-Str. 5, 09599 Freiberg, Germany) ,  Nielsch Kornelius (Leibniz IFW Dresden, Helmholtzstr. 20, 01069 Dresden, Germany) ,  Nielsch Kornelius (TU Dresden, Institute of Materials Science, 01062 Dresden, Germany) ,  Woodcock Thomas George (Leibniz IFW Dresden, Helmholtzstr. 20, 01069 Dresden, Germany)
資料名： Journal of Alloys and Compounds  (Journal of Alloys and Compounds)
巻： 897  ページ： Null  発行年： 2022年 
JST資料番号： D0083A  ISSN： 0925-8388  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： 最大エネルギー製品,(BH)_max≧42kJm-3を有するMnAl-C-Ni磁石を,熱間押出粉砕メルトスパンリボンによって製造した。紡糸したままのリボン(1μm≦d≦6μm)中の柱状結晶粒の小さい直径は,押出前の700°Cでの保持過程中に形成されるτ相結晶粒の最大サイズを制限した。高ホイール速度で製造したリボンから製造した押出材料における非再結晶領域の不在は,このより小さな初期τ相粒径(1μm≦d≦2μm)に起因し,消磁曲線の正方形因子の増強をもたらした。Copyright 2022 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： *再結晶 ,  *磁石 ,  *粉体 ,  粒径 ,  *紡糸 ,  *溶融紡糸 ,  消磁 ,  結晶粒 ,  熱間押出 ,  柱状晶
準シソーラス用語： τ相 , 【Automatic Indexing@JST】

著者キーワード (4件)： 硬磁石 ,  MnAl-C ,  溶融紡糸 ,  押出

分類 (1件)： 磁気的性質  (WB02020J)

タイトルに関連する用語 (7件)： 粉末 ,  溶融紡糸 ,  リボン ,  押出 ,  Ni ,  磁石 ,  再結晶