硫酸溶液中の高温Ir-Ni-Ta-(B)非晶質合金の優れた耐食性【JST・京大機械翻訳】

Superior corrosion resistance of high-temperature Ir-Ni-Ta-(B) amorphous alloy in sulfuric acid solution

著者 (9件)： Yang Xiaodong (Anhui Key Laboratory of High-Performance Non-Ferrous Metal Materials, Anhui Polytechnic University, Wuhu 241000, China) ,  Yang Xiaodong (CAS Key Laboratory of Magnetic Materials and Devices, and Zhejiang Province Key Laboratory of Magnetic Materials and Application Technology, Ningbo Institute of Materials Technology & Engineering, Chinese Academy of Sciences, Ningbo, Zhejiang 315201, China) ,  Gao Meng (CAS Key Laboratory of Magnetic Materials and Devices, and Zhejiang Province Key Laboratory of Magnetic Materials and Application Technology, Ningbo Institute of Materials Technology & Engineering, Chinese Academy of Sciences, Ningbo, Zhejiang 315201, China) ,  Liu Yanhui (Institute of Physics, Chinese Academy of Sciences, Beijing 100190, China) ,  Li Jinlong (Key Laboratory of Marine Materials and Related Technologies, Zhejiang Key Laboratory of Marine Materials and Protective Technologies, Ningbo Institute of Materials Technology and Engineering, Chinese Academy of Sciences, Ningbo 315201, China) ,  Huang Yan (CAS Key Laboratory of Magnetic Materials and Devices, and Zhejiang Province Key Laboratory of Magnetic Materials and Application Technology, Ningbo Institute of Materials Technology & Engineering, Chinese Academy of Sciences, Ningbo, Zhejiang 315201, China) ,  Wang Gang (Anhui Key Laboratory of High-Performance Non-Ferrous Metal Materials, Anhui Polytechnic University, Wuhu 241000, China) ,  Wang Jun-Qiang (CAS Key Laboratory of Magnetic Materials and Devices, and Zhejiang Province Key Laboratory of Magnetic Materials and Application Technology, Ningbo Institute of Materials Technology & Engineering, Chinese Academy of Sciences, Ningbo, Zhejiang 315201, China) ,  Huo Juntao (CAS Key Laboratory of Magnetic Materials and Devices, and Zhejiang Province Key Laboratory of Magnetic Materials and Application Technology, Ningbo Institute of Materials Technology & Engineering, Chinese Academy of Sciences, Ningbo, Zhejiang 315201, China)
資料名： Corrosion Science  (Corrosion Science)
巻： 200  ページ： Null  発行年： 2022年 
JST資料番号： B0135B  ISSN： 0010-938X  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： 本研究では,酸性溶液中の高温Ir基非晶質合金の腐食挙動と基礎となる機構を系統的に調べた。Ir-Ni-Ta-B非晶質合金は,低い不動態電流密度と広い不動態電位範囲を特徴とする優れた耐食性を有する隙間腐食挙動を示した。メタロイド成分上のH+とH_2対の高交換電流密度は不動態化元素の活性析出を加速し,不動態皮膜の急速な形成につながることが分かった。硫酸溶液中で,Ir,Ta5+およびNi3+酸化物を含む形成された不動態膜は耐食性を著しく増加させた。Copyright 2022 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： *高温 ,  電位 ,  分極 ,  *イリジウム ,  酸化物 ,  *耐食性 ,  不動態 ,  不動態化 ,  不動態皮膜 ,  電流密度 ,  半金属 ,  *非晶質合金
準シソーラス用語： 交換電流密度 ,  酸性溶液 ,  腐食挙動 , 【Automatic Indexing@JST】

著者キーワード (5件)： Ir基非晶質合金 ,  耐食性 ,  酸性溶液 ,  分極 ,  受動膜

分類 (1件)： 腐食  (WB03030B)

タイトルに関連する用語 (6件)： 硫酸溶液 ,  Ir ,  Ni ,  Ta ,  非晶質合金 ,  耐食性