硫酸腐食下の粗ポーラスコンクリートの浸透性進展モデル【JST・京大機械翻訳】

Permeability evolution model of coarse porous concrete under sulphuric acid corrosion

著者 (8件)： Qiu Peitao (School of Civil Engineering, Xuzhou University of Technology, Xuzhou, Jiangsu 221018, China) ,  Zhang Lianying (School of Civil Engineering, Xuzhou University of Technology, Xuzhou, Jiangsu 221018, China) ,  Li Yan (School of Civil Engineering, Xuzhou University of Technology, Xuzhou, Jiangsu 221018, China) ,  Li Bing (School of Civil Engineering, Xuzhou University of Technology, Xuzhou, Jiangsu 221018, China) ,  Zhu Jiong (School of Civil Engineering, Xuzhou University of Technology, Xuzhou, Jiangsu 221018, China) ,  Ma Chao (School of Civil Engineering, Xuzhou University of Technology, Xuzhou, Jiangsu 221018, China) ,  Bi Xiaoxi (School of Civil Engineering, Xuzhou University of Technology, Xuzhou, Jiangsu 221018, China) ,  Yu Yang (School of Civil Engineering, Xuzhou University of Technology, Xuzhou, Jiangsu 221018, China)
資料名： Construction and Building Materials  (Construction and Building Materials)
巻： 326  ページ： Null  発行年： 2022年 
JST資料番号： T0560A  ISSN： 0950-0618  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： 酸腐食の間の粗い多孔性コンクリート(CPC)のミクロ構造と透水性進展を研究することは,都市浸水と建築スポンジ都市の解決のために非常に重要である。本研究では,硫酸溶液中でセメント量を変えてCPCsについて透過率とミクロ走査試験を行った。凝縮係数を体積要素材料導関数で定義し,速度モデルを確立した。結果は,硫酸溶液のpHの低下とセメント含有量の増加に伴い,CPCの透過性が減少し,水和と腐食の両方を促進することを示した。Copyright 2022 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： *腐食 ,  セメント ,  *コンクリート ,  *硫酸 ,  透水性 ,  *気泡コンクリート ,  都市 ,  水和 ,  浸水 ,  透過率 ,  *浸透率 ,  導関数 ,  反応速度論
準シソーラス用語： スポンジ ,  *酸腐食 , 【Automatic Indexing@JST】

著者キーワード (5件)： 硫酸腐食 ,  粗ポーラスコンクリート ,  反応速度論 ,  セメント ,  浸透性

分類 (1件)： モルタル,コンクリート  (RA06042H)

タイトルに関連する用語 (6件)： 硫酸 ,  腐食 ,  ポーラスコンクリート ,  浸透性 ,  進展 ,  モデル