650°Cにおけるインコネル706の低サイクル疲れ挙動【JST・京大機械翻訳】

Low cycle fatigue behavior of Inconel 706 at 650 °C

著者 (5件)： Oh Hojun (Department of Materials Engineering and Convergence Technology, RECAPT, Gyeongsang National University, Jinju, 52828, Republic of Korea) ,  Kim Soyoung (Department of Materials Engineering and Convergence Technology, RECAPT, Gyeongsang National University, Jinju, 52828, Republic of Korea) ,  Kim Jung Gi (Department of Materials Engineering and Convergence Technology, RECAPT, Gyeongsang National University, Jinju, 52828, Republic of Korea) ,  Taleghani Firooz (Lockheed Martin Global Inc., Sacheon, 52529, Republic of Korea) ,  Kim Sangshik (Department of Materials Engineering and Convergence Technology, RECAPT, Gyeongsang National University, Jinju, 52828, Republic of Korea)
資料名： Journal of Materials Research and Technology  (Journal of Materials Research and Technology)
巻： 17  ページ： 2624-2635  発行年： 2022年 
JST資料番号： W3532A  ISSN： 2238-7854  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： 鍛造ディスクの中心と周辺から調製した2段階と3段階時効インコネル706(IN706)試料の低サイクル疲労(LCF)挙動を,650°CとR比-1で調べた。IN706合金のLCFに対する耐性は,同じ時効条件に対して,IN718合金よりも650°Cで約半分大きかった。2段階および3段階時効IN706試験片間の高温Coffin-Manson関係は,微細構造におけるかなりの差にもかかわらず,互いに類似していた。破面解析は,炭化物のクラスタが2段階および3段階時効試料の両方に対して亀裂発生のサイトを提供することを示唆した。各試験片の疲れ亀裂成長モードは粒界と粒内であったが,各モードに対して異なる大きさであった。試料作製の位置に依存して,IN706合金の鍛造ブロックを形成し,LCF抵抗の顕著な差は見られなかった。IN706合金の開始および伝播機構に及ぼす結晶粒界,炭化物のクラスタおよび針状η小板のバンドの役割を,詳細な破面およびミクログラフィック解析に基づいて議論した。Copyright 2022 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： 円板 ,  結晶粒界 ,  高温 ,  合金 ,  時効 ,  *低サイクル疲れ ,  砥粒 ,  炭化物 ,  鍛造 ,  クラスタ ,  試料調製 ,  *インコネル ,  亀裂発生 ,  疲れ亀裂成長
準シソーラス用語： IN718 , 【Automatic Indexing@JST】

著者キーワード (4件)： インコネル706 ,  低サイクル疲れ ,  高温 ,  老化

分類 (2件)： 金属材料  (HC05020S) ,  機械的性質  (WB02030U)

タイトルに関連する用語 (3件)： インコネル ,  低サイクル疲れ ,  挙動