有望な水素貯蔵のためのY修飾MoS_2単分子層:DFT研究【JST・京大機械翻訳】

Y-decorated MoS₂ monolayer for promising hydrogen storage: A DFT study

著者 (11件)： Liu Hongying (School of Physics and Electronic Information, Hubei Key Laboratory for Processing and Application of Catalytic Materials, Huanggang Normal University, Huanggang 438000, PR China) ,  Yang Shulin (School of Physics and Electronic Information, Hubei Key Laboratory for Processing and Application of Catalytic Materials, Huanggang Normal University, Huanggang 438000, PR China) ,  Yang Shulin (Faculty of Physics and Electronic Sciences, Hubei Key Laboratory of Ferro & Piezoelectric Materials and Devices, Hubei University, Wuhan 430062, PR China) ,  Lei Gu (School of Physics and Electronic Information, Hubei Key Laboratory for Processing and Application of Catalytic Materials, Huanggang Normal University, Huanggang 438000, PR China) ,  Xu Miaojing (School of Physics and Electronic Information, Hubei Key Laboratory for Processing and Application of Catalytic Materials, Huanggang Normal University, Huanggang 438000, PR China) ,  Xu Huoxi (School of Physics and Electronic Information, Hubei Key Laboratory for Processing and Application of Catalytic Materials, Huanggang Normal University, Huanggang 438000, PR China) ,  Lan Zhigao (School of Physics and Electronic Information, Hubei Key Laboratory for Processing and Application of Catalytic Materials, Huanggang Normal University, Huanggang 438000, PR China) ,  Wang Zhao (Faculty of Physics and Electronic Sciences, Hubei Key Laboratory of Ferro & Piezoelectric Materials and Devices, Hubei University, Wuhan 430062, PR China) ,  Xiong Juan (Faculty of Physics and Electronic Sciences, Hubei Key Laboratory of Ferro & Piezoelectric Materials and Devices, Hubei University, Wuhan 430062, PR China) ,  Gu Haoshuang (School of Physics and Electronic Information, Hubei Key Laboratory for Processing and Application of Catalytic Materials, Huanggang Normal University, Huanggang 438000, PR China) ,  Gu Haoshuang (Faculty of Physics and Electronic Sciences, Hubei Key Laboratory of Ferro & Piezoelectric Materials and Devices, Hubei University, Wuhan 430062, PR China)
資料名： International Journal of Hydrogen Energy  (International Journal of Hydrogen Energy)
巻： 47  号： 24  ページ： 12096-12106  発行年： 2022年 
JST資料番号： B0192B  ISSN： 0360-3199  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： 構築したY修飾MoS_2の水素貯蔵性能を第一原理密度汎関数理論(DFT)計算により調べた。Yは-4.82eVの吸着エネルギーでMoS_2単分子層上に安定に修飾され,その絶対値はバルクYの凝集エネルギーより高かった。導入したH_2はY修飾MoS_2と強く相互作用し,伸長結合長と妥当な吸着エネルギーはそれぞれ0.792Åと-0.904eVであった。最大吸着に4つのH_2があり,平均吸着エネルギーが-0.387eVであるY修飾MoS_2に貯蔵された。さらに,各側に完全なY被覆率を有するMoS_2の水素重量容量を4.56wt%に改善でき,平均吸着エネルギーは-0.295eVであった。本研究は,Yで修飾したMoS_2が,有望な重量密度でH_2を効果的に貯蔵する可能性のある材料であることを明らかにした。Copyright 2022 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： 吸着 ,  相互作用 ,  密度 ,  *水素 ,  核間距離 ,  *単分子層 ,  容量 ,  計算 ,  重量測定 ,  *水素吸蔵 ,  絶対値 ,  凝集エネルギー ,  密度汎関数法 ,  第一原理 ,  吸着エネルギー

著者キーワード (5件)： Y修飾 ,  MoS_2 ,  水素貯蔵 ,  DFT ,  重量測定能力

分類 (1件)： 気体燃料の輸送,供給,貯蔵  (YE02060M)

タイトルに関連する用語 (5件)： 水素貯蔵 ,  修飾 ,  単分子層 ,  DFT ,  研究