Al-空気電池用の自己腐食を抑制したスプレーフォーミング市販アルミニウム合金アノード【JST・京大機械翻訳】

Spray-formed commercial aluminum alloy anodes with suppressed self-corrosion for Al-Air batteries

著者 (6件)： Ren Jianming (School of Materials Science and Engineering, Shanghai Jiao Tong University, Shanghai, 200240, PR China) ,  Liu Tao (School of Materials Science and Engineering, Shanghai Jiao Tong University, Shanghai, 200240, PR China) ,  Zhang Jiao (School of Materials Science and Engineering, Shanghai Jiao Tong University, Shanghai, 200240, PR China) ,  Jiang Min (School of Materials Science and Engineering, Shanghai Jiao Tong University, Shanghai, 200240, PR China) ,  Dong Qing (School of Materials Science and Engineering, Shanghai Jiao Tong University, Shanghai, 200240, PR China) ,  Fu Chaopeng (School of Materials Science and Engineering, Shanghai Jiao Tong University, Shanghai, 200240, PR China)
資料名： Journal of Power Sources  (Journal of Power Sources)
巻： 524  ページ： Null  発行年： 2022年 
JST資料番号： B0703B  ISSN： 0378-7753  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： スプレー成形法とそれに続く熱処理によって製造された市販の7050Al合金を,自己腐食を大きく抑えたAl-空気電池のアノードとして研究した。作製したAl合金アノードの微細構造を特性化し,鋳造7050Al合金のそれらと比較した。スプレー形成Alアノードは,より微細な結晶粒とより低い体積分率と第2相の不連続分布を有し,より小さな自己腐食率をもたらした。変形および熱処理の後,噴霧成形Al合金は,第二相の体積分率および低角粒界の高い割合を示した。従って,調製したAlアノードを有するAl-空気電池は,大きな比容量と高い作動電圧を示した。本研究は,市販のAl合金が,スプレーフォーミングと適切な熱処理の組合せによって,Al-空気電池のアノードとして使用できることを示した。Copyright 2022 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： 結晶粒界 ,  電圧 ,  微細構造 ,  *腐食 ,  *アルミニウム ,  *アルミニウム合金 ,  鋳造 ,  腐食速度 ,  結晶粒 ,  *空気電池 ,  不連続性 ,  キャラクタリゼーション ,  *スプレーフォーミング ,  *アノード
準シソーラス用語： 比容量 , 【Automatic Indexing@JST】

著者キーワード (4件)： Al合金アノード ,  スプレーフォーミング ,  自己腐食 ,  Al-空気電池