凝集体上の微生物誘起CaCO_3保護層によるアルカリ-シリカ反応の緩和【JST・京大機械翻訳】

Mitigation of alkali-silica reaction by microbially induced CaCO₃ protective layer on aggregates

著者 (5件)： Lu Chun-Hua (Faculty of Civil Engineering and Mechanics, Jiangsu University, Zhenjiang, Jiangsu 212013, China) ,  Bu Sen-zhuang (Faculty of Civil Engineering and Mechanics, Jiangsu University, Zhenjiang, Jiangsu 212013, China) ,  Shahin Mohamed A. (School of Civil and Mechanical Engineering, Curtin University, Perth 6102, Australia) ,  Zheng Yu-long (Faculty of Civil Engineering and Mechanics, Jiangsu University, Zhenjiang, Jiangsu 212013, China) ,  Cheng Liang (Institute of Environmental Health and Ecological Security, School of Environment and Safety Engineering, Jiangsu University, Zhenjiang, Jiangsu 212013, China)
資料名： Construction and Building Materials  (Construction and Building Materials)
巻： 328  ページ： Null  発行年： 2022年 
JST資料番号： T0560A  ISSN： 0950-0618  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： アルカリ-シリカ反応(ASR)によって生成された水膨潤ゲルは,通常コンクリートの膨張と亀裂を引き起こし,機械的性質の低下をもたらす。ASRは,環境に優しい微生物誘起炭酸塩沈殿(MICP)技術によってある程度阻害でき,それは,尿素分解細菌,セメンテーション溶液(尿素+塩化カルシウム)および凝集体の混合による処理後に,活性凝集体表面上にCaCO_3結晶の保護層を形成することができる。生成したCaCO_3は処理回数と共に増加し,ASRのより良い保護と改善された抑制をもたらした。処理骨材(6回)を用いたモルタル棒試験片は,可視表面亀裂なしで,55%による膨張の著しい減少を示した。さらに,微小亀裂の減少により,モルタルバー試料の圧縮強度は約36%増加した。Copyright 2022 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： 亀裂 ,  膨潤 ,  *微生物 ,  コンクリート ,  骨材 ,  塩化カルシウム ,  沈殿 ,  ゲル ,  *二酸化ケイ素 ,  モルタル ,  炭酸塩 ,  圧縮強さ ,  微小亀裂 ,  *凝集体 ,  ウレア化合物

著者キーワード (4件)： アルカリ-シリカ反応 ,  微生物誘導炭酸塩沈殿 ,  阻害 ,  コンクリート膨張