優れた機械的性能を有する木材-エポキシ高分子複合材料の調製と機械的破壊解析【JST・京大機械翻訳】

Preparation and mechanical failure analysis of wood-epoxy polymer composites with excellent mechanical performances

著者 (6件)： Guo Dengkang (Research Institute of Wood Industry, Chinese Academy of Forestry, Beijing, 100091, China) ,  Guo Nai (Research Institute of Wood Industry, Chinese Academy of Forestry, Beijing, 100091, China) ,  Fu Feng (Research Institute of Wood Industry, Chinese Academy of Forestry, Beijing, 100091, China) ,  Yang Sheng (Research Institute of Wood Industry, Chinese Academy of Forestry, Beijing, 100091, China) ,  Li Gaiyun (Research Institute of Wood Industry, Chinese Academy of Forestry, Beijing, 100091, China) ,  Chu Fuxiang (Institute of Chemical Industry of Forest Products, Chinese Academy of Forestry, 210037, Nanjing, China)
資料名： Composites. Part B. Engineering  (Composites. Part B. Engineering)
巻： 235  ページ： Null  発行年： 2022年 
JST資料番号： W0437B  ISSN： 1359-8368  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： 本研究では,優れた機械的特性を有する木材-エポキシ高分子複合材料(WEPC)を,植林木材のセル空洞にエポキシ単量体を導入した後,機械的負荷の下で応力-歪システムを調整することによって調製した。WEPCの曲げ強さ,弾性率,圧縮強度および衝撃強度は,それぞれ110.3%,86.5%,137.3%および110.6%まで向上した。曲げ強度(140.5MPa)は,強度クラスTB20(98MPa)を超えており,これはバラ材より高かった。機械的強度の改善は,主に,エポキシポリマーおよび強化セル壁との負荷を共有することによる応力集中特性の変化に起因した。強化された靭性は,細胞壁のマルチレベル構造間の「亀裂の伝播」と同様に,縦セル分裂の増加に起因した。WEPCの機械的破壊機構は,木材ベース複合材料の設計のための参照として使用できる。Copyright 2022 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： 応力集中 ,  亀裂 ,  弾性係数 ,  *木材 ,  靱性 ,  細胞壁 ,  単量体 ,  衝撃強さ ,  圧縮強さ ,  曲げ強さ ,  機械的強度
準シソーラス用語： *PMC【材料】 ,  *破壊解析 ,  破壊機構 ,  応力-歪 , 【Automatic Indexing@JST】

著者キーワード (5件)： 木材-エポキシポリマ複合材料 ,  機械的性質 ,  細胞壁 ,  細胞空洞 ,  故障メカニズム

分類 (2件)： 強化プラスチックの成形  (YH04060J) ,  エポキシ樹脂  (YH07040I)

タイトルに関連する用語 (5件)： 機械的性能 ,  木材 ,  高分子複合材料 ,  調製 ,  破壊解析