800~900°Cでの1気圧O_2における3/5wt%Alまたは8/15wt%Crを含む4つの三元Co-20Ni基合金のスケーリング挙動【JST・京大機械翻訳】

Scaling behavior of four ternary Co-20Ni-based alloys containing 3/5 wt% Al or 8/15 wt% Cr in 1 Atm O₂ at 800-900 °C

著者 (8件)： Lv Y.L. (School of Energy & Power Engineering, Changsha University of Science & Technology, Changsha, China) ,  Ren Y.J. (School of Energy & Power Engineering, Changsha University of Science & Technology, Changsha, China) ,  Wang W. (Institute of Metal Research, Wencui Road 62, 110016 Shenyang, China) ,  Zhou L.B. (School of Energy & Power Engineering, Changsha University of Science & Technology, Changsha, China) ,  Chen J. (School of Energy & Power Engineering, Changsha University of Science & Technology, Changsha, China) ,  Huang J. (School of Energy & Power Engineering, Changsha University of Science & Technology, Changsha, China) ,  Tao M.S. (School of Energy & Power Engineering, Changsha University of Science & Technology, Changsha, China) ,  Niu Y. (School of Energy & Power Engineering, Changsha University of Science & Technology, Changsha, China)
資料名： Corrosion Science  (Corrosion Science)
巻： 199  ページ： Null  発行年： 2022年 
JST資料番号： B0135B  ISSN： 0010-938X  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： 2つのCo-20Ni-yAl(y=3,5wt%),2つのCo-20Ni-xCr(x=8,15wt%)およびCo-20Ni合金の1atmO_2の酸化を80~900°Cで研究した。900°Cで酸化したCo-20Ni-15Crを除いて,全ての三元合金は両温度で二元合金Co-20Niより急速に酸化された。900°Cでの酸化によって,三元合金Co-20Ni-15Crの表面にのみ,薄い保護酸化物層が形成された。他の全ての場合において,スケールはCo-Ni酸化物の外層とスピネルと混合されたCo-Ni酸化物の内部層および内部酸化のゾーンを含んだ。Copyright 2022 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： *合金 ,  スピネル ,  スケール ,  コバルト合金 ,  酸化物 ,  高温酸化 ,  内部酸化 ,  二元合金 ,  三元合金 ,  酸化層

著者キーワード (4件)： Co基合金 ,  BSEM ,  Cの高温酸化 ,  C保護スケール