種々のCr含有量と関連特性を持つ鋳造合金IN625におけるδ相析出【JST・京大機械翻訳】

δ phase precipitation in cast alloy IN625 with varied Cr content and associated properties

著者 (6件)： Mu Yiqiang (Civil Aviation College, Shenyang Aerospace University, Shenyang, China; Institute of Metal Research, Chinese Academy of Sciences, Shenyang, China) ,  Cheng Yuting (Civil Aviation College, Shenyang Aerospace University, Shenyang, China) ,  Han Fei (Civil Aviation College, Shenyang Aerospace University, Shenyang, China) ,  Wang Changshuai (Institute of Metal Research, Chinese Academy of Sciences, Shenyang, China) ,  Cui Xu (Civil Aviation College, Shenyang Aerospace University, Shenyang, China) ,  Xu Qinsi (Civil Aviation College, Shenyang Aerospace University, Shenyang, China; Institute of Metal Research, Chinese Academy of Sciences, Shenyang, China)
資料名： Emerging Materials Research  (Emerging Materials Research)
巻： XXXX  号： XXXX  ページ： 1-5  発行年： 2022年 
JST資料番号： W5107A  ISSN： 2046-0147  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： 鋳造合金IN625を最近開発し,700°C級先進超超臨界プラントの候補材料として評価した。鋳造合金IN625のδ相析出と機械的性質に及ぼすクロム(Cr)の影響を明らかにするために,異なるクロム添加の鋳造合金IN625の時効処理実験を行った。750°Cでの時効後の鋳造合金IN625中のδ相の析出は,クロム含有量によってほとんど影響されないことが明らかになった。鋳造合金IN625の引張特性はクロム含有量に鈍感であったが,δ相に敏感であった。応力破断試験は,時効合金の破断時間が固溶体合金のそれらと比較して増加することを示した。さらに,δ相の分率が18から35%に増加したとき,400および375MPaでの応力破断寿命において,それぞれ異なる傾向が現れた。Please refer to the publisher for the copyright holders. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： 機械的性質 ,  *合金 ,  固溶体 ,  時効 ,  *析出 ,  プラント ,  破断 ,  クロム ,  時効処理 ,  *δ相 ,  超臨界
準シソーラス用語： 引張特性 ,  応力破断 ,  *鋳造合金 , 【Automatic Indexing@JST】

著者キーワード (3件)： 合金 ,  材料構造 ,  機械的性質

分類 (2件)： 機械的性質  (WB02030U) ,  変態組織,加工組織  (WB01030N)

タイトルに関連する用語 (4件)： Cr含有量 ,  鋳造合金 ,  δ相 ,  析出