AISI 304上のHVOF溶射WC-10Co-4Cr+GNP被覆に及ぼすレーザ集合組織前処理の影響【JST・京大機械翻訳】

Influence of laser texturing pre-treatment on HVOF-sprayed WC-10Co-4Cr+GNP coatings on AISI 304

著者 (4件)： Kumar Vijay (Industrial and Production Engineering Department, Dr B R Ambedkar National Institute of Technology Jalandhar, Punjab, -144011, India) ,  Verma Rajeev (Industrial and Production Engineering Department, Dr B R Ambedkar National Institute of Technology Jalandhar, Punjab, -144011, India) ,  Chauhan Kundan (Industrial and Production Engineering Department, Dr B R Ambedkar National Institute of Technology Jalandhar, Punjab, -144011, India) ,  Kumar Rakesh (Industrial and Production Engineering Department, Dr B R Ambedkar National Institute of Technology Jalandhar, Punjab, -144011, India)
資料名： Surface Topography: Metrology and Properties  (Surface Topography: Metrology and Properties)
巻： 10  号： 1  ページ： 015052 (19pp)  発行年： 2022年 
JST資料番号： W5576A  ISSN： 2051-672X  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： 高速度酸素燃料(HVOF)は,サーメット原料粉末による純合金表面の保護被覆のための最も重要な溶射技術の一つである。本論文では,HVOFコーティング前のグリットブラストをレーザテクスチャリングによって置換し,AISI304鋼基板上の堆積WC-10Co-4Cr+3%グラフェンナノプレートレット(GNPs)のより良い機械的インターロッキングのための特定の粗さと決定論的空洞パターンを作成した。2つの形状;第1は,直径(d)100μmとピッチ(p)120μmの円形テクスチャリング(CT)であり,第2は,側面(s)100μmと側面(ss)距離120μmの三角形テクスチャリング(TT)を使用した。種々の試験手段;表面粗さ,XRD解析,FESEM画像解析,EDS分析,格子歪と残留応力,スクラッチ試験,被覆とベース基板断面のVickers硬さ試験,および滑り摩耗挙動のピンオンディスク試験を行った。これらの被覆特性評価の後,格子歪と残留応力は著しく減少し,断面の微小硬さは向上し,被覆の接着強度は強化され,被覆表面上の低い滑り摩耗率が観察された。表面への原料粉末の均一な分布,しかし,TT表面上のより高い多孔性は,FESEM画像解析と,より高い荷重でのスクラッチ試験中に観察される多数の亀裂を示した。Please refer to the publisher for the copyright holders. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： X線回折 ,  亀裂 ,  合金 ,  格子歪 ,  サーメット ,  残留応力 ,  *集合組織 ,  微小硬さ ,  *被覆 ,  *溶射 ,  接着強さ ,  テキスチャード加工 ,  画像分析 ,  引かき試験 ,  滑り摩耗

分類 (2件)： 溶射  (WC08030N) ,  金属材料へのセラミック被覆  (YC02050V)

タイトルに関連する用語 (5件)： HVOF溶射 ,  WC ,  レーザ ,  集合組織 ,  前処理