予備加硫と多層積層法による配向グラファイトを有するスケーラブル高熱伝導性シリコーンゴム複合材料【JST・京大機械翻訳】

A scalable highly thermal conductive silicone rubber composite with orientated graphite by pre-vulcanizing and multilayer stacking method

著者 (12件)： Zhang Rong (Hubei Provincial Key Laboratory of Green Materials for Light Industry, New Materials and Manufacturing Talent Introduction and Innovation Demonstration Base, Hubei University of Technology, Wuhan, China) ,  Liu Zhuohang (Hubei Provincial Key Laboratory of Green Materials for Light Industry, New Materials and Manufacturing Talent Introduction and Innovation Demonstration Base, Hubei University of Technology, Wuhan, China) ,  Sun Zhijian (School of Materials Science and Engineering, Georgia Institute of Technology, Atlanta, USA) ,  He Xuehang (Hubei Provincial Key Laboratory of Green Materials for Light Industry, New Materials and Manufacturing Talent Introduction and Innovation Demonstration Base, Hubei University of Technology, Wuhan, China) ,  Lin Qianhui (Hubei Provincial Key Laboratory of Green Materials for Light Industry, New Materials and Manufacturing Talent Introduction and Innovation Demonstration Base, Hubei University of Technology, Wuhan, China) ,  Xiang Yifan (Hubei Provincial Key Laboratory of Green Materials for Light Industry, New Materials and Manufacturing Talent Introduction and Innovation Demonstration Base, Hubei University of Technology, Wuhan, China) ,  Fang Xiang (Hubei Provincial Key Laboratory of Green Materials for Light Industry, New Materials and Manufacturing Talent Introduction and Innovation Demonstration Base, Hubei University of Technology, Wuhan, China) ,  Li Siqi (Hubei Provincial Key Laboratory of Green Materials for Light Industry, New Materials and Manufacturing Talent Introduction and Innovation Demonstration Base, Hubei University of Technology, Wuhan, China) ,  Fu Xudong (Hubei Provincial Key Laboratory of Green Materials for Light Industry, New Materials and Manufacturing Talent Introduction and Innovation Demonstration Base, Hubei University of Technology, Wuhan, China) ,  Liu Qingting (Hubei Provincial Key Laboratory of Green Materials for Light Industry, New Materials and Manufacturing Talent Introduction and Innovation Demonstration Base, Hubei University of Technology, Wuhan, China) ,  Hu Shengfei (Hubei Provincial Key Laboratory of Green Materials for Light Industry, New Materials and Manufacturing Talent Introduction and Innovation Demonstration Base, Hubei University of Technology, Wuhan, China) ,  Ping Wong Ching (School of Materials Science and Engineering, Georgia Institute of Technology, Atlanta, USA)
資料名： Composites. Part A. Applied Science and Manufacturing  (Composites. Part A. Applied Science and Manufacturing)
巻： 157  ページ： Null  発行年： 2022年 
JST資料番号： E0231D  ISSN： 1359-835X  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： シリコーンゴム(SR)ベースの熱伝導性複合材料は,熱抵抗性熱界面材料(TIM)の良い候補である。熱伝導率(TC)を増加させ,コア層におけるSRの加硫の困難さとして厚い試料を得る挑戦である。ここでは,配向Gr(O-SR/Gr)を有する高熱伝導性および10mmのSR/グラファイト(Gr)を,予備加硫および多層積層ホットプレスによって調製した。Grの緻密な構造と優れた配向を有するよく硬化した厚い複合材料を得た。O-SR/Grの面内TCは,66.67wt%Grで13.93W/(m・K)に達し,一方,予備加硫のない試料は,サンプル間でボイドを示した。Grの高密度複合材料と優れた配向は,Foygelモデルに適合した界面熱抵抗(ITR)を減少させた。また,それらは,実際の温暖化プロセスおよび200°Cまでの顕著な熱抵抗の間,急速な昇温速度を示した。この知見は,大規模での高熱伝導率複合材料の効率的な設計に対するインスピレーションを提供するかもしれない。Copyright 2022 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： 熱抵抗 ,  熱伝導率 ,  複合材料 ,  耐熱性 ,  ホットプレス ,  *グラファイト ,  *加硫 ,  モデル ,  加熱速度 ,  熱特性 ,  *配向 ,  多層 ,  温暖化
準シソーラス用語： 界面熱抵抗 ,  *熱伝導性 , 【Automatic Indexing@JST】

著者キーワード (4件)： A.高分子マトリックス複合材料(PMCs) ,  E.プレフォーミング ,  B.指向性配向 ,  B.熱特性

分類 (2件)： 充填剤,補強材  (YH05030J) ,  物理的性質一般  (YH02021U)

タイトルに関連する用語 (7件)： 加硫 ,  多層 ,  配向 ,  グラファイト ,  高熱伝導性 ,  シリコーン ,  ゴム複合材料