炭素/ガラスハイブリッド繊維強化ポリマー棒の圧縮特性分析と強度対細長比関係予測【JST・京大機械翻訳】

Compressive property analysis and strength versus slenderness ratio relation prediction for carbon/glass hybrid fiber reinforced polymer bars

著者 (7件)： Gao Danying (School of Civil Engineering, Zhengzhou University, Zhengzhou 450001, Henan, China) ,  Gao Danying (School of Water Conservancy Engineering, Zhengzhou University, Zhengzhou, 450001, Henan, China) ,  Zhang Yu (School of Civil Engineering, Zhengzhou University, Zhengzhou 450001, Henan, China) ,  Fang Dong (School of Civil Engineering, Zhengzhou University, Zhengzhou 450001, Henan, China) ,  Ding Chong (School of Civil Engineering, Zhengzhou University, Zhengzhou 450001, Henan, China) ,  Yan Huanhuan (School of Water Conservancy Engineering, Zhengzhou University, Zhengzhou, 450001, Henan, China) ,  Ji Dongdong (School of Water Conservancy Engineering, Zhengzhou University, Zhengzhou, 450001, Henan, China)
資料名： Construction and Building Materials  (Construction and Building Materials)
巻： 317  ページ： Null  発行年： 2022年 
JST資料番号： T0560A  ISSN： 0950-0618  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： 本論文では,全305炭素/ガラスハイブリッド繊維強化ポリマー(HFRP)棒試験片を圧縮下で試験し,炭素繊維の表面形態,体積率および分布パターン,繊維の全体積率および細長比の影響を系統的に調べた。その結果,炭素/ガラス-HFRP棒の圧縮強度は,炭素繊維の種々の置換率に対して,種々の還元を示した。エンド定着のない炭素/ガラス-HFRP棒試料の圧縮強度は,エンド定着の試験片と比較して平均14.0%減少した。最後に,圧縮強度と細長比の間の関係を,異なる特性を有する炭素/ガラス-HFRP棒試験片について予測した。Copyright 2022 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： *ガラス ,  細長比 ,  炭素繊維 ,  圧縮強さ ,  *繊維強化プラスチック ,  圧縮性 ,  体積率 ,  置換率
準シソーラス用語： 表面形態 , 【Automatic Indexing@JST】

著者キーワード (6件)： ハイブリッド繊維強化ポリマー棒 ,  圧縮特性 ,  関係予測 ,  細長比 ,  表面構成 ,  体積分率