グラフェン強化Cu/0.5CeO_230Cr電気接点材料の調製と特性【JST・京大機械翻訳】

Preparation and properties of graphene reinforced Cu/0.5CeO₂30Cr electrical contact materials

著者 (30件)： Liu Shuang (School of Materials Science and Engineering, Henan University of Science and Technology, Luoyang, 471023, China) ,  Liu Shuang (Provincial and Ministerial Co-construction of Collaborative Innovation Center for Non-ferrous Metal New Materials and Advanced Processing Technology, Luoyang, 471023, China) ,  Liu Shuang (Henan Key Laboratory of Nonferrous Materials Science and Processing Technology, Luoyang, 471023, China) ,  Li Lihua (School of Materials Science and Engineering, Henan University of Science and Technology, Luoyang, 471023, China) ,  Li Lihua (Provincial and Ministerial Co-construction of Collaborative Innovation Center for Non-ferrous Metal New Materials and Advanced Processing Technology, Luoyang, 471023, China) ,  Li Lihua (Henan Key Laboratory of Nonferrous Materials Science and Processing Technology, Luoyang, 471023, China) ,  Zhou Meng (School of Materials Science and Engineering, Henan University of Science and Technology, Luoyang, 471023, China) ,  Zhou Meng (Provincial and Ministerial Co-construction of Collaborative Innovation Center for Non-ferrous Metal New Materials and Advanced Processing Technology, Luoyang, 471023, China) ,  Zhou Meng (Henan Key Laboratory of Nonferrous Materials Science and Processing Technology, Luoyang, 471023, China) ,  Liang Shengli (School of Materials Science and Engineering, Henan University of Science and Technology, Luoyang, 471023, China) ,  Liang Shengli (Provincial and Ministerial Co-construction of Collaborative Innovation Center for Non-ferrous Metal New Materials and Advanced Processing Technology, Luoyang, 471023, China) ,  Liang Shengli (Henan Key Laboratory of Nonferrous Materials Science and Processing Technology, Luoyang, 471023, China) ,  Zhang Yi (School of Materials Science and Engineering, Henan University of Science and Technology, Luoyang, 471023, China) ,  Zhang Yi (Provincial and Ministerial Co-construction of Collaborative Innovation Center for Non-ferrous Metal New Materials and Advanced Processing Technology, Luoyang, 471023, China) ,  Zhang Yi (Henan Key Laboratory of Nonferrous Materials Science and Processing Technology, Luoyang, 471023, China) ,  Huang Jinliang (School of Materials Science and Engineering, Henan University of Science and Technology, Luoyang, 471023, China) ,  Huang Jinliang (Provincial and Ministerial Co-construction of Collaborative Innovation Center for Non-ferrous Metal New Materials and Advanced Processing Technology, Luoyang, 471023, China) ,  Huang Jinliang (Henan Key Laboratory of Nonferrous Materials Science and Processing Technology, Luoyang, 471023, China) ,  Tian Baohong (School of Materials Science and Engineering, Henan University of Science and Technology, Luoyang, 471023, China) ,  Tian Baohong (Provincial and Ministerial Co-construction of Collaborative Innovation Center for Non-ferrous Metal New Materials and Advanced Processing Technology, Luoyang, 471023, China) ,  Tian Baohong (Henan Key Laboratory of Nonferrous Materials Science and Processing Technology, Luoyang, 471023, China) ,  Geng Yongfeng (School of Materials Science and Engineering, Henan University of Science and Technology, Luoyang, 471023, China) ,  Geng Yongfeng (Provincial and Ministerial Co-construction of Collaborative Innovation Center for Non-ferrous Metal New Materials and Advanced Processing Technology, Luoyang, 471023, China) ,  Geng Yongfeng (Henan Key Laboratory of Nonferrous Materials Science and Processing Technology, Luoyang, 471023, China) ,  Liu Yong (School of Materials Science and Engineering, Henan University of Science and Technology, Luoyang, 471023, China) ,  Liu Yong (Provincial and Ministerial Co-construction of Collaborative Innovation Center for Non-ferrous Metal New Materials and Advanced Processing Technology, Luoyang, 471023, China) ,  Liu Yong (Henan Key Laboratory of Nonferrous Materials Science and Processing Technology, Luoyang, 471023, China) ,  Jia Yanlin (School of Materials Science and Engineering, Central South University, Changsha, 410083, China) ,  Li Xu (Center for Advanced Measurement Science, National Institute of Metrology, Beijing, 100029, China) ,  Volinsky Alex A. (Department of Mechanical Engineering, University of South Florida, 4202 E. Fowler Ave. ENG030, Tampa, 33620, USA)
資料名： Vacuum  (Vacuum)
巻： 195  ページ： Null  発行年： 2022年 
JST資料番号： E0347A  ISSN： 0042-207X  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： 高強度と電気伝導率を有するグラフェン強化Cu/CeO_2Cr電気接点材料を設計した。酸化グラフェン(GO)を,改良Hummers法を用いて調製した。GO,セリアナノ粒子,銅およびクロムの複合粉末を凍結乾燥によって調製した。GO-Cu/0.5CeO_230Cr電気接点材料を放電プラズマ焼結により作製した。RamanとX線光電子分光法(XPS)キャラクタリゼーションの結果は,焼結過程で酸化グラフェンが還元グラフェン酸化物(RGO)に転換されることを示した。さらに,SEMとTEMキャラクタリゼーションの結果は,CeO_2ナノ粒子がマトリックス中に均一に分散し,転位の移動を妨げ,マトリックスの強度を改善し,Cr_3C_2を形成するためにCrと結合した少量の炭素原子がCr_3C_2を形成し,界面結合を強化することを示した。Cu/0.5CeO_230Cr複合材料と比較して,0.5wt%と1.0wt%GOを含む2つの複合材料の電気伝導率,硬度,引張強度,および溶接抵抗は両方とも改善され,0.5GO-Cu/0.5CeO_230Cr複合材料はより良い溶接抵抗を有した。Copyright 2022 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： 界面 ,  焼結 ,  電気伝導率 ,  凍結乾燥 ,  クロム ,  *銅 ,  溶接 ,  *接点材料 ,  酸化セリウム ,  *電気接点 ,  引張強さ ,  ナノ粒子 ,  放電プラズマ焼結 ,  *グラフェン
準シソーラス用語： 酸化グラフェン , 【Automatic Indexing@JST】

著者キーワード (5件)： 銅マトリックス複合材料 ,  酸化グラフェン ,  セリアナノ粒子 ,  その場形成 ,  電気接点

分類 (2件)： 炭素とその化合物  (YB02060D) ,  ろう付  (WC07050C)

タイトルに関連する用語 (5件)： グラフェン ,  強化 ,  Cu ,  電気接点材料 ,  調製