炭化物強化TiNbTaZrHf複合材料の高温機械特性と変形挙動【JST・京大機械翻訳】

High-temperature mechanical properties and deformation behavior of carbides reinforced TiNbTaZrHf composite

著者 (7件)： Li Xiaofeng (School of Materials Science and Engineering, North University of China, Taiyuan 030051, China) ,  Li Xiaofeng (State Key Laboratory of Powder Metallurgy, Central South University, Changsha 410083, China) ,  Fu Ao (State Key Laboratory of Powder Metallurgy, Central South University, Changsha 410083, China) ,  Cao Yuankui (State Key Laboratory of Powder Metallurgy, Central South University, Changsha 410083, China) ,  Cao Yuankui (Foshan (Southern China) Institute for New Materials, Foshan 528010, China) ,  Xu Shenghang (College of Materials Science and Engineering, Zhejiang University of Technology, Hangzhou 310014, China) ,  Gao Shenghan (State Key Laboratory of Powder Metallurgy, Central South University, Changsha 410083, China)
資料名： Journal of Alloys and Compounds  (Journal of Alloys and Compounds)
巻： 894  ページ： Null  発行年： 2022年 
JST資料番号： D0083A  ISSN： 0925-8388  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： 耐火性高エントロピー合金(RHEAs)は,高温での優れた機械的性質のため,高温構造材料の分野で広い展望を有する。本研究では,新しいTiNbTaZrHf系複合材料を粉末冶金その場法で製作した。炭化物の導入によって,TiNbTaZrHf基複合材料は,室温で2620MPaの超高降伏強度を示した。一方,複合材料は1000°Cで508MPaの高い強度を維持した。顕著な強度改善は,高い体積分率を有する分散炭化物に起因する耐荷重効果に起因し,一方,炭化物の粒界破壊は塑性不安定性の原因となる。温度が1200°Cに上昇すると,降伏強さは著しく低下する。荷重支持効果の弱化と粒界滑りの活性化が強度減少の主な理由であり,一方,マトリックスと炭化物の間の界面剥離が主要な破壊挙動になる。Copyright 2022 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： *機械的性質 ,  *高温 ,  複合材料 ,  *炭化物 ,  粉末冶金 ,  降伏強さ ,  粒界破壊 ,  耐荷力 ,  粒界滑り
準シソーラス用語： 界面剥離 ,  *変形挙動 ,  高エントロピー合金 ,  破壊挙動 ,  塑性不安定性 ,  強度低下 , 【Automatic Indexing@JST】

著者キーワード (5件)： 耐火性高エントロピー合金 ,  微細構造 ,  粉末冶金 ,  機械的性質 ,  破壊挙動

分類 (2件)： セラミック・磁器の性質  (YC03030G) ,  分散強化合金  (WE04030R)

タイトルに関連する用語 (5件)： 炭化物 ,  強化 ,  複合材料 ,  機械特性 ,  変形挙動