ロールツーロールグラビア印刷による大面積,高性能単層カーボンナノチューブ(SWCNT)ベースヒータ膜の作製【JST・京大機械翻訳】

Preparation of large-area, high-performance single-walled carbon nanotube (SWCNT)-based heater films by roll-to-roll gravure printing

著者 (13件)： Zhang Qin (College of microelectronics, Sipailou Campus, Southeast University, Xuanwu District, Nanjing, Jiangsu 210096, People’s Republic of China) ,  Zhang Qin (Printable Electronics Research Centre, Division of Nanodevices and Related Nanomaterials, Suzhou Institute of Nano-Tech and Nano-Bionics, Chinese Academy of Sciences, 398 Ruoshui Road, Suzhou 215123, People’s Republic of China) ,  Zhang Qin (School of Nano-Tech and Nano-Bionics, University of Science and Technology of China, No. 398 Ruoshui Road, SEID, Suzhou Industrial Park, Suzhou, Jiangsu Province 215123, People’s Republic of China) ,  Ren Yunfei (Printable Electronics Research Centre, Division of Nanodevices and Related Nanomaterials, Suzhou Institute of Nano-Tech and Nano-Bionics, Chinese Academy of Sciences, 398 Ruoshui Road, Suzhou 215123, People’s Republic of China) ,  Ren Yunfei (School of Nano-Tech and Nano-Bionics, University of Science and Technology of China, No. 398 Ruoshui Road, SEID, Suzhou Industrial Park, Suzhou, Jiangsu Province 215123, People’s Republic of China) ,  Wang Zhenguo (School of Nano-Tech and Nano-Bionics, University of Science and Technology of China, No. 398 Ruoshui Road, SEID, Suzhou Industrial Park, Suzhou, Jiangsu Province 215123, People’s Republic of China) ,  Chen Xiaolian (School of Nano-Tech and Nano-Bionics, University of Science and Technology of China, No. 398 Ruoshui Road, SEID, Suzhou Industrial Park, Suzhou, Jiangsu Province 215123, People’s Republic of China) ,  Portilla Luis (Frontier Institute of Chip and System, Fudan University, Shanghai 200433, People’s Republic of China) ,  Sun Litao (College of microelectronics, Sipailou Campus, Southeast University, Xuanwu District, Nanjing, Jiangsu 210096, People’s Republic of China) ,  Zhang Dongyu (Printable Electronics Research Centre, Division of Nanodevices and Related Nanomaterials, Suzhou Institute of Nano-Tech and Nano-Bionics, Chinese Academy of Sciences, 398 Ruoshui Road, Suzhou 215123, People’s Republic of China) ,  Zhang Dongyu (School of Nano-Tech and Nano-Bionics, University of Science and Technology of China, No. 398 Ruoshui Road, SEID, Suzhou Industrial Park, Suzhou, Jiangsu Province 215123, People’s Republic of China) ,  Zhao Jianwen (Printable Electronics Research Centre, Division of Nanodevices and Related Nanomaterials, Suzhou Institute of Nano-Tech and Nano-Bionics, Chinese Academy of Sciences, 398 Ruoshui Road, Suzhou 215123, People’s Republic of China) ,  Zhao Jianwen (School of Nano-Tech and Nano-Bionics, University of Science and Technology of China, No. 398 Ruoshui Road, SEID, Suzhou Industrial Park, Suzhou, Jiangsu Province 215123, People’s Republic of China)
資料名： Flexible and Printed Electronics  (Flexible and Printed Electronics)
巻： 7  号： 1  ページ： 015007 (10pp)  発行年： 2022年 
JST資料番号： W5556A  ISSN： 2058-8585  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： 本研究では,ロールツーロール(R2R)グラビア印刷技術により,ポリエチレンテレフタレート基板上に大面積高性能単層カーボンナノチューブ(SWCNT)系導電性薄膜を調製するための環境に優しい高速方法を開発した。SWCNTまたはSWCNT/銀ナノワイヤ(AgNW)膜から成る大面積(16cm×32cm)導電性膜をR2Rグラビア印刷法により初めて作製した。伝導率,透過率,機械的柔軟性および加熱能力を詳細に評価した。例えば,SWCNT薄膜とSWCNT/AgNW複合膜の正方形抵抗は69.92と17.44Ω/□であり,550nmの波長での光透過率はそれぞれ50.70%と66.77%であった。一方,調製したSWCNTおよびSWCNT/AgNW複合膜は優れた加熱安定性,温度均一性および曲げ抵抗を示した。複合膜は3.5mmの曲率半径で6000の曲げサイクルに耐え,低い駆動電圧(6V),速い加熱応答(15s以内)および加熱速度(約4.933°Cs-1)で100°Cまでの温度を得た。これらの特性は複合膜の機械的および加熱特性の改善におけるSWCNTsの可能性を反映しており,これは低電力,大面積,フレキシブルおよびカスタマイズ可能な電子デバイスに対して有望である。Please refer to the publisher for the copyright holders. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： 電圧 ,  薄膜 ,  *グラビア印刷 ,  波長 ,  ポリエチレンテレフタレート ,  加熱速度 ,  透過率 ,  複合膜 ,  *単層カーボンナノチューブ ,  ナノワイヤ
準シソーラス用語： 電子素子 ,  駆動電圧 ,  *ロール・ツー・ロール方式 ,  導電膜 ,  光透過率 ,  銀ナノワイヤ ,  伝導率 , 【Automatic Indexing@JST】

分類 (2件)： 炭素とその化合物  (YB02060D) ,  その他の無機化合物の薄膜  (BK14060A)

タイトルに関連する用語 (8件)： ロールツーロール ,  グラビア印刷 ,  大面積 ,  高性能 ,  単層カーボンナノチューブ ,  SWCNT ,  ヒータ ,  作製