1073Kにおけるその場TiC/Ni複合材料の酸化機構【JST・京大機械翻訳】

Oxidation mechanism of in-situ TiC/Ni composites at 1073 K

著者 (6件)： Zhao Ziyan (School of Materials Science and Engineering, Shandong University of Science and Technology, Qingdao 266590, Shandong, China) ,  Yu Xianghui (School of Materials Science and Engineering, Shandong University of Science and Technology, Qingdao 266590, Shandong, China) ,  Wang Chao (School of Materials Science and Engineering, Shandong University of Science and Technology, Qingdao 266590, Shandong, China) ,  Yao Shuyu (School of Materials Science and Engineering, Shandong University of Science and Technology, Qingdao 266590, Shandong, China) ,  Qi Qian (School of Materials Science and Engineering, Shandong University of Science and Technology, Qingdao 266590, Shandong, China) ,  Wang Lujie (State Key Laboratory of Solid Lubrication, Lanzhou Institute of Chemical Physics, Chinese Academy of Sciences, Lanzhou 730000, China)
資料名： Corrosion Science  (Corrosion Science)
巻： 194  ページ： Null  発行年： 2022年 
JST資料番号： B0135B  ISSN： 0010-938X  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： 反応性焼結により調製したその場TiC/Ni複合材料の1073Kでの酸化挙動は放物線速度論に従った。酸化活性化エネルギーは210±30kJ・mol-1であり,ルチルによるO拡散のそれに近かった。複合材料上に形成された酸化物スケールは,2つの層を含む:連続外層は,上部TiO_2+NiTiO_3+NiOとnetherTiO_2,およびNiマトリックス中に分散したTiO_2島から成る内部層から成る。酸化プロセスは,TiとNiの外向き拡散とOの内向き拡散によって決定され,後者が主要な役割を果たし,外層より内部層の速い成長速度をもたらす。Copyright 2022 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： 活性化エネルギー ,  *酸化 ,  複合材料 ,  *チタン ,  *ニッケル ,  酸化膜 ,  ルチル ,  速度論 ,  反応焼結 ,  成長速度
準シソーラス用語： *酸化機構 ,  酸化挙動 , 【Automatic Indexing@JST】

著者キーワード (2件)： その場TiC/Ni複合材料 ,  酸化機構

分類 (2件)： 腐食  (WB03030B) ,  セラミック・磁器の性質  (YC03030G)

タイトルに関連する用語 (4件)： TiC ,  Ni ,  複合材料 ,  酸化機構