J-GLOBAL ID：202202288606966494   整理番号：22A0956033

リチウムイオン電池のための高レートおよび長サイクル寿命アノードとしてのFeドープK_0.8Ti_1.73Li_0.27O_4@rGOの合理的設計【JST・京大機械翻訳】

Rational design of Fe-doped K_0.8Ti_1.73Li_0.27O₄@rGO as a high-rate and long-cycle-life anode for lithium-ion batteries

著者 (11件)： Hou Lijuan (Key Laboratory of Material Physics of the Ministry of Education, School of Physics and Microelectronics, Zhengzhou University, Zhengzhou 450052, People’s Republic of China) ,  Zhang Limin (Key Laboratory of Material Physics of the Ministry of Education, School of Physics and Microelectronics, Zhengzhou University, Zhengzhou 450052, People’s Republic of China) ,  Zang Jinhao (Key Laboratory of Material Physics of the Ministry of Education, School of Physics and Microelectronics, Zhengzhou University, Zhengzhou 450052, People’s Republic of China) ,  Shen Weixia (Key Laboratory of Material Physics of the Ministry of Education, School of Physics and Microelectronics, Zhengzhou University, Zhengzhou 450052, People’s Republic of China) ,  Zhang Taiyi (State Key Laboratory of Biobased Material and Green Papermaking, Department of Bioengineering, Qilu University of Technology (Shandong Academy of Sciences), Jinan 250353, People’s Republic of China) ,  Huang Xiaowen (State Key Laboratory of Biobased Material and Green Papermaking, Department of Bioengineering, Qilu University of Technology (Shandong Academy of Sciences), Jinan 250353, People’s Republic of China) ,  Yuan Huiyu (Henan Key Laboratory of High Temperature Functional Ceramics, School of Materials Science and Engineering, Zhengzhou University, Zhengzhou 450052, People’s Republic of China) ,  Kong Dezhi (Key Laboratory of Material Physics of the Ministry of Education, School of Physics and Microelectronics, Zhengzhou University, Zhengzhou 450052, People’s Republic of China) ,  Wang Ye (Key Laboratory of Material Physics of the Ministry of Education, School of Physics and Microelectronics, Zhengzhou University, Zhengzhou 450052, People’s Republic of China) ,  Li Xinjian (Key Laboratory of Material Physics of the Ministry of Education, School of Physics and Microelectronics, Zhengzhou University, Zhengzhou 450052, People’s Republic of China) ,  Xu Tingting (Key Laboratory of Material Physics of the Ministry of Education, School of Physics and Microelectronics, Zhengzhou University, Zhengzhou 450052, People’s Republic of China)
資料名： Journal of Physics. D. Applied Physics  (Journal of Physics. D. Applied Physics)
巻： 55  号： 23  ページ： 234002 (10pp)  発行年： 2022年 
JST資料番号： B0092B  ISSN： 0022-3727  CODEN： JPAPBE  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： K_0.8Ti_1.73Li_0.27O_4(KLTO)は,リチウムイオン電池(LIB)のための重要なチタンベースアノード材料であり,その非毒性,低コスト,および高い安全性性能を考慮して,炭素質材料の代替になることが期待される。しかし,それは低い伝導率と妨害されたLiイオン拡散のため,高い充放電速度において低い比容量に悩まされる。本研究では,簡単な静電集合プロセスとそれに続くLIBのアノードとしてのその高速および長サイクル寿命性能に従って調製したFeドープKLTO@rGO(Fe-KLTO@rGO)複合材料を得た。Fe-KLTO@rGO複合試料は,電流密度1C(1C=175mA g-1)および50Cにおいて,それぞれ330および105mAh g-1の優れた比容量を有していた。さらに,Fe-KLTO@rGO複合試料は50Cの速度で3000サイクルの長いサイクルを実行でき,比容量は127mAh/gに留まった。Please refer to the publisher for the copyright holders. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： 複合材料 ,  *リチウム ,  *ドーピング ,  イオン拡散 ,  電流密度 ,  炭素材 ,  *サイクル寿命 ,  充放電サイクル ,  *アノード ,  *リチウムイオン電池
準シソーラス用語： アノード材料【電池】 ,  充放電 ,  比容量 ,  伝導率 , 【Automatic Indexing@JST】

分類 (1件)： 二次電池  (YB04030K)

タイトルに関連する用語 (7件)： リチウムイオン電池 ,  レート ,  サイクル寿命 ,  アノード ,  Fe ,  ドープ ,  設計