HAYNES282Ni基超合金のクリープ-疲れ応答,破壊モードおよび変形機構:滞留時間と時間の影響【JST・京大機械翻訳】

Creep-Fatigue Response, failure mode and deformation mechanism of HAYNES 282 Ni based superalloy: Effect of dwell position and time

著者 (6件)： Mukherjee Shreya (Department of Metallurgical and Materials Engineering, Indian Institute of Technology Kharagpur, Kharagpur 721302, India) ,  Kumar Kar Sujoy (Department of Metallurgical and Materials Engineering, Indian Institute of Technology Kharagpur, Kharagpur 721302, India) ,  Sivaprasad S. (CSIR - National Metallurgical Laboratory, Jamshedpur 831007, India) ,  Tarafder Soumitra (CSIR - National Metallurgical Laboratory, Jamshedpur 831007, India) ,  Viswanathan G.B. (Center for Electron Microscopy and Analysis, Ohio State University, Columbus, OH 43212, USA) ,  Fraser H.L. (Center for Electron Microscopy and Analysis, Ohio State University, Columbus, OH 43212, USA)
資料名： International Journal of Fatigue  (International Journal of Fatigue)
巻： 159  ページ： Null  発行年： 2022年 
JST資料番号： D0802B  ISSN： 0142-1123  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： HAYNES-282のクリープ疲れ(C-F)応答を,対応する変形ミクロ機構および破壊モードとともに,ドウェル位置と時間の関数として提示した。全歪反転点を超えた非弾性歪における慣性効果を初めて報告した。材料中の損傷(DC-F)は,dwell,圧縮-dwellおよび引張-dwellの両方の順に減少することがわかった。DC-F,サイクル当りの有効応力緩和,および歪エネルギー密度は,寿命と良く相関することが分かった。剪断からOrowanループへの変形機構の変化は,滞留位置の関数として損傷の違いを説明する。HAYNES282は歪硬化挙動に固有の異方性を示し,圧縮荷重の下ではより高い。圧縮ドウェルは,同じセグメントの歪硬化の有益な効果を無効にする滞留時間-軟化により,そのような材料でより損傷すると仮定した。破壊は,ドウェル位置と時間に依存して,粒内または粒界破壊のいずれかの支配を伴う混合モードを通して起こる。Copyright 2022 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： *クリープ ,  剪断 ,  *変形 ,  *滞留時間 ,  緩和現象 ,  引張 ,  圧縮荷重 ,  粒界破壊 ,  混合モード ,  有効応力 ,  クリープ疲れ ,  *破壊モード
準シソーラス用語： *変形機構 ,  ひずみエネルギー密度 ,  非弾性歪 , 【Automatic Indexing@JST】

著者キーワード (5件)： クリープ疲労 ,  滞留時間と位置 ,  変形機構 ,  故障モード ,  HAYNES 282

分類 (1件)： 金属材料  (HC05020S)

タイトルに関連する用語 (5件)： クリープ ,  疲れ ,  応答 ,  破壊モード ,  滞留時間