CFRPEK/A6061-T6 FLJハイブリッド継手を強化するためのフェムト秒レーザ作製マイクロ/ナノ界面構造【JST・京大機械翻訳】

Femtosecond laser fabricated micro/nano interfacial structures to strengthen CFRPEEK/A6061-T6 FLJ hybrid joints

著者 (5件)： Bi Xiaoyang (School of Mechanical & Automotive Engineering, South China University of Technology, Guangzhou, 510641, PR China) ,  Wang Zhenmin (School of Mechanical & Automotive Engineering, South China University of Technology, Guangzhou, 510641, PR China) ,  Xu Mengjia (School of Mechanical Engineering and Automation, Northeastern University, No. 11 Wenhua Road, Shenyang, 110819, PR China) ,  Xu Mengjia (Foshan Graduate School of Northeastern University, No. 2 Zhihui Road, Foshan, 528300, PR China) ,  Li Xiaopeng (College of Materials Science and Technology, Nanjing University of Science and Technology, Nanjing, 210014, PR China)
資料名： Composites. Part B. Engineering  (Composites. Part B. Engineering)
巻： 231  ページ： Null  発行年： 2022年 
JST資料番号： W0437B  ISSN： 1359-8368  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： 金属-熱可塑性ハイブリッド継手は,近年,先進飛行車両の軽量化に広く使用されている。本研究では,フェムト秒レーザを用いて,A6061-T6(6061)表面上のマイクロストリップとナノ粒子の二重スケール階層構造を構築し,摩擦重ね接合(FLJ)により炭素繊維強化ポリエーテルケトン(CFRPEEK)と安定なハイブリッド継手を作製した。CFRPEEK/6061の結合強度に及ぼすフェムト秒レーザ改質の影響を,実験方法と有限要素解析(FEA)によって明らかにした。結果は,有効な機械的インターロッキングがCFRPEEK/6061 FLJ継手の結合強度の強化を引き起こすことを示した。さらに,フェムト秒レーザ改質の加工パラメータを調整することによって,6061表面は超疎水性に発展し,ボイドと亀裂のない完全なCFRPEEK/6061界面をもたらし,19.40MPaの最大結合強度に対応した。Copyright 2022 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： *界面 ,  亀裂 ,  数値解析 ,  *継手【接合】 ,  軽量化 ,  *アルミニウム合金 ,  マイクロストリップ線路 ,  炭素繊維 ,  熱塑性 ,  飛翔 ,  付着強さ ,  ナノ粒子 ,  *フェムト秒レーザ
準シソーラス用語： 有限要素解析 ,  超疎水性 ,  *A6061 ,  *ナノ界面 , 【Automatic Indexing@JST】

著者キーワード (5件)： CFRPEK ,  摩擦重ね接合 ,  フェムト秒レーザ ,  有限要素モデリング ,  機械的性質

分類 (2件)： 強化プラスチックの成形  (YH04060J) ,  接合部  (HD03080V)

タイトルに関連する用語 (6件)： A6061 ,  継手 ,  強化 ,  フェムト秒レーザ ,  作製 ,  界面構造