MnCoGe基合金導入によるMg-9Al-1Znマグネシウム合金の熱膨張挙動の調整と機械的特性の促進【JST・京大機械翻訳】

Tuning the thermal expansion behavior and promoting the mechanical properties of Mg-9Al-1Zn magnesium alloys by the introduction of MnCoGe-based alloys

著者 (7件)： Wu Sujuan (College of Materials Science and Engineering, Chongqing University, Chongqing 400044, China) ,  Zhou Daiqi (College of Materials Science and Engineering, Chongqing University, Chongqing 400044, China) ,  Huang Yadong (College of Materials Science and Engineering, Chongqing University, Chongqing 400044, China) ,  Wang Ke (College of Materials Science and Engineering, Chongqing University, Chongqing 400044, China) ,  Song Jiangfeng (College of Materials Science and Engineering, Chongqing University, Chongqing 400044, China) ,  Dong Zhihua (College of Materials Science and Engineering, Chongqing University, Chongqing 400044, China) ,  Jiang Bin (College of Materials Science and Engineering, Chongqing University, Chongqing 400044, China)
資料名： Scripta Materialia  (Scripta Materialia)
巻： 214  ページ： Null  発行年： 2022年 
JST資料番号： B0915A  ISSN： 1359-6462  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： MgとAl/Cu合金における熱膨張の不整合は,継手界面で剥離または破壊を引き起こし,さらにそれらの耐用年数と実用化を制限する。負の熱膨張材料を組み合わせるとMg合金の熱膨張は減少するが,延性は破壊される。本研究では,Mg-9Al-1ZnMg合金とMnCoGe基合金の組み合わせによってこの課題を克服した。7wt%以下のMn_0.98CoGeの添加はCu合金の熱膨張の整合係数と中程度の強度と塑性を示した。予測値との不整合により,熱膨張調節と機械的性質改善の両方に関する臨界メカニズムが,二次相と金属結合界面に起因することを示した。低い熱膨張と良好な機械的特性を有するこれらのMg合金は,電子パッケージングと精密分野に有用である。Copyright 2022 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： 延性 ,  界面 ,  塑性 ,  機械的性質 ,  *合金 ,  *熱膨張 ,  *アルミニウム ,  *マグネシウム ,  銅合金 ,  *マグネシウム合金 ,  臨界 ,  不整合 ,  耐用年数
準シソーラス用語： 予測値 ,  負の熱膨張 , 【Automatic Indexing@JST】

分類 (1件)： 機械的性質  (WB02030U)

タイトルに関連する用語 (6件)： Mg ,  マグネシウム合金 ,  熱膨張 ,  挙動 ,  機械的特性 ,  促進