海水脱塩における強化ホウ素除去のためのポリアミド膜の表面工学設計【JST・京大機械翻訳】

Surface engineering design of polyamide membranes for enhanced boron removal in seawater desalination

著者 (7件)： Wang Shuhao (College of Chemical and Biological Engineering, Zhejiang University, Hangzhou, 310027, China) ,  Bing Shaosuo (College of Chemical and Biological Engineering, Zhejiang University, Hangzhou, 310027, China) ,  Bing Shaosuo (Department of Organic Membrane, Jiuwu Hi-Tech Company, Nanjing, 211808, China) ,  Zhang Haoyong (Qdbeson Environmental Engineering Company, Qingdao, 266107, China) ,  Zhou Yong (Center for Membrane and Water Science & Technology, Zhejiang University of Technology, Hangzhou, 310014, China) ,  Zhang Lin (College of Chemical and Biological Engineering, Zhejiang University, Hangzhou, 310027, China) ,  Gao Congjie (Center for Membrane and Water Science & Technology, Zhejiang University of Technology, Hangzhou, 310014, China)
資料名： Journal of Membrane Science  (Journal of Membrane Science)
巻： 651  ページ： Null  発行年： 2022年 
JST資料番号： E0669A  ISSN： 0376-7388  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： ホウ素(B)除去用の優れたポリアミド(PA)海水逆浸透(SWRO)膜は重要な挑戦である。ここでは,界面重合の反応速度を制御することによって,SWRO膜のホウ素除去と脱塩性能を改善するための容易な表面工学設計戦略を開発した。PA骨格の表面を覆っているオリゴマの官能基と密度を調整して,膜の選択性を強化したPA活性層内の細孔径と水素結合相互作用を減少させた。設計した膜は95.34%の高いホウ素除去率を示し,一方,99.8%のNaCl排除と許容できる水フラックスを示した。本研究は,優れたSWRO膜の設計のための基本的なフレームワークを提供し,また,界面重合に基づくポリアミド膜の形成と構造-特性関係に対するいくつかの洞察を与えた。Copyright 2022 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： 水素結合 ,  反応速度 ,  *ポリアミド ,  逆浸透 ,  塩化ナトリウム ,  界面重合 ,  除去 ,  オリゴマ ,  *淡水化 ,  細孔径 ,  活性層 ,  物質流束
準シソーラス用語： 官能基 ,  構造特性相関 ,  水フラックス ,  *ホウ素除去 , 【Automatic Indexing@JST】

著者キーワード (5件)： ホウ素除去 ,  表面工学設計 ,  ポリアミドオリゴマ ,  逆浸透 ,  界面重合

分類 (2件)： 膜分離  (XD02120Z) ,  ポリアミド  (YH07080A)

タイトルに関連する用語 (6件)： 海水脱塩 ,  強化 ,  ホウ素除去 ,  ポリアミド ,  表面工学 ,  設計