文献

J-GLOBAL ID：202202298547463923   整理番号：22A1094658

レーザ粉末ベッド融合を用いて製造されたAl-Si合金の降伏強さの負の歪速度感受性【JST・京大機械翻訳】

Negative strain rate sensitivity of yield strength of Al-Si alloy additive-manufactured using laser powder bed fusion

著者 (5件)： Takata Naoki (Department of Materials Process Engineering, Graduate School of Engineering, Nagoya University, Furo-cho, Chikusa-ku, Nagoya 464-8603 Japan) ,  Liu Mulin (Department of Materials Process Engineering, Graduate School of Engineering, Nagoya University, Furo-cho, Chikusa-ku, Nagoya 464-8603 Japan) ,  Suzuki Asuka (Department of Materials Process Engineering, Graduate School of Engineering, Nagoya University, Furo-cho, Chikusa-ku, Nagoya 464-8603 Japan) ,  Kobashi Makoto (Department of Materials Process Engineering, Graduate School of Engineering, Nagoya University, Furo-cho, Chikusa-ku, Nagoya 464-8603 Japan) ,  Kato Masaki (Aichi Center for Industry and Science Technology, 1267-1 Akiai, Yakusa-cho, Toyota 470-0356 Japan)
資料名： Scripta Materialia  (Scripta Materialia)
巻： 213  ページ： Null  発行年： 2022年 
JST資料番号： B0915A  ISSN： 1359-6462  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： 本論文は,レーザ粉末床溶融(L-PBF)プロセスを用いて製造したAl-12%Si合金の機械的挙動の予想外の発見を報告する。製造したままの試料は,引張変形の初期段階(歪で3%以下)で,流れ応力の負の歪速度感受性を有した。後熱処理試料は正の歪速度感受性を示し,これらの試料のいずれも鋸歯状応力-歪曲線を示さず,Portevin-LeChatelier効果とは異なる機構を示した。透過電子顕微鏡は,周囲温度で変形した製造したままの試料中のα-Alマトリックスの過飽和固溶体内部のナノサイズSi相の動的析出を明らかにした。動的に析出したSi相は導入された転位と相互作用し,塑性変形の初期段階における流れ応力を強化した。動的析出は,引張変形の初期段階(降伏強さを含む)での流れ応力の負の歪速度感受性に寄与することができた。Copyright 2022 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： *合金 ,  析出 ,  相互作用 ,  流れ応力 ,  *粉体 ,  *ケイ素 ,  アルミニウム合金 ,  過飽和固溶体 ,  後熱処理 ,  *降伏強さ ,  塑性変形 ,  引張変形 ,  透過型電子顕微鏡 ,  応力歪曲線
準シソーラス用語： *歪速度感受性 , 【Automatic Indexing@JST】

著者キーワード (5件)： レーザ粉体層核融合 ,  選択的レーザ融解 ,  アルミニウム合金 ,  歪速度感受性 ,  動的降水

分類 (1件)： 機械的性質  (WB02030U)

タイトルに関連する用語 (7件)： レーザ ,  粉末 ,  ベッド ,  融合 ,  Al-Si合金 ,  降伏強さ ,  歪速度感受性