Effects of loading mode and water chemistry on stress corrosion crack growth behavior of 316L HAZ and weld metal materials in high temperature pure water

高温純水中の316LHAZ及び溶接金属材料の応力腐食割れ成長に対する荷重方式及び水の特性の影響

Author (6)： LU Zhanpeng (Fracture and Reliability Res. Inst., Fac. of Engineering, Tohoku Univ., Aramaki Aoba, Aoba-ku, Sendai 980-8579, JPN) ,  SHOJI Tetsuo (Fracture and Reliability Res. Inst., Fac. of Engineering, Tohoku Univ., Aramaki Aoba, Aoba-ku, Sendai 980-8579, JPN) ,  TAKEDA Yoichi (Fracture and Reliability Res. Inst., Fac. of Engineering, Tohoku Univ., Aramaki Aoba, Aoba-ku, Sendai 980-8579, JPN) ,  ITO Yuzuru (Fracture and Reliability Res. Inst., Fac. of Engineering, Tohoku Univ., Aramaki Aoba, Aoba-ku, Sendai 980-8579, JPN) ,  KAI Akira (Fracture and Reliability Res. Inst., Fac. of Engineering, Tohoku Univ., Aramaki Aoba, Aoba-ku, Sendai 980-8579, JPN) ,  TSUCHIYA Nobuhisa (Fracture and Reliability Res. Inst., Fac. of Engineering, Tohoku Univ., Aramaki Aoba, Aoba-ku, Sendai 980-8579, JPN)
Material： Corrosion Science  (International Journal of the Science and Practice of Corrosion and Protection)
Volume： 50  Issue： 3  Page： 625-638  Publication year： Mar. 2008 
JST Material Number： B0135B  ISSN： 0010-938X  Document type： Article
Article type： 原著論文  Country of issue： United Kingdom (GBR)  Language： ENGLISH (EN)

Thesaurus term： *stress corrosion cracking ,  growth rate ,  *austenitic stainless steel ,  *weld zone ,  welded heat affected zone ,  weld metal ,  intergranular crack ,  dendrite(crystal) ,  dissolved oxygen ,  hydrogen ,  electrode potential ,  charge transfer ,  mass transfer ,  crack tip ,  strain rate
Semi thesaurus term： AISI316L

JST classification (2)： Corrosion  (WB03030B) ,  Weld zone  (WC07100I)

Terms in the title (7)： 純水 ,  溶接 ,  金属材料 ,  応力腐食割れ ,  成長 ,  荷重 ,  水