The dependency of the crack growth rate on the loading pattern and temperature in stress corrosion cracking of strain-hardened 316L stainless steels in a simulated BWR environment

シミュレートBWR雰囲気での歪硬化316Lステンレス鋼の応力腐食割れにおける亀裂成長速度の負荷パターンと温度に対する依存性

Author (5)： LU Zhanpeng (Fracture and Reliability Res. Inst., Tohoku Univ., Aramaki Aoba 6-6-01, Aoba-ku, Sendai 980-8579, JPN) ,  SHOJI Tetsuo (Fracture and Reliability Res. Inst., Tohoku Univ., Aramaki Aoba 6-6-01, Aoba-ku, Sendai 980-8579, JPN) ,  TAKEDA Yoichi (Fracture and Reliability Res. Inst., Tohoku Univ., Aramaki Aoba 6-6-01, Aoba-ku, Sendai 980-8579, JPN) ,  ITO Yuzuru (Fracture and Reliability Res. Inst., Tohoku Univ., Aramaki Aoba 6-6-01, Aoba-ku, Sendai 980-8579, JPN) ,  YAMAZAKI Seiya (Fracture and Reliability Res. Inst., Tohoku Univ., Aramaki Aoba 6-6-01, Aoba-ku, Sendai 980-8579, JPN)
Material： Corrosion Science  (International Journal of the Science and Practice of Corrosion and Protection)
Volume： 50  Issue： 3  Page： 698-712  Publication year： Mar. 2008 
JST Material Number： B0135B  ISSN： 0010-938X  Document type： Article
Article type： 原著論文  Country of issue： United Kingdom (GBR)  Language： ENGLISH (EN)

Thesaurus term： *stress corrosion cracking ,  crack propagation ,  *growth rate ,  austenitic stainless steel ,  warm working ,  load curve ,  activation energy ,  rate-limiting ,  temperature dependence ,  yield strength ,  precrack
Semi thesaurus term： *AISI316L

JST classification (1)： Corrosion  (WB03030B)

Terms in the title (7)： BWR ,  雰囲気 ,  歪硬化 ,  316Lステンレス鋼 ,  応力腐食割れ ,  亀裂成長速度 ,  依存性