Art

J-GLOBAL ID：201002278369975227   Reference number：10A0859174

Fatigue Crack Growth and its Tip Opening Displacement in Cartridge Brass

73黄銅平板における疲労き裂の進展およびき裂先端開口変位

Author (1)： HAYASHI MORIHITO (東海大 工)
Material： 銅と銅合金  (Journal of Japan Institute of Copper)
Volume： 49  Page： 283-287  Publication year： Aug. 01, 2010 
JST Material Number： S0603A  ISSN： 1347-7234  Document type： Article
Article type： 原著論文  Country of issue： Japan (JPN)  Language： JAPANESE (JA)

Thesaurus term： *brass ,  flat plate ,  *mechanical property ,  fatigue crack ,  fatigue crack growth ,  crack opening displacement ,  crack tip ,  formula ,  CT specimen ,  fatigue crack growth rate ,  fracture surface ,  scanning electron microscope ,  microscope ,  striation(material phenomenon) ,  organization ,  stress intensity factor ,  fracture toughness ,  constant
Semi thesaurus term： predicting expression ,  digital microscope ,  inside tissue ,  material constant

JST classification (1)： Mechanical properties  (WB02030U)

Reference (10)：

• Hayashi, M.: Sixth International Conference on Low Cycle Fatigue-LCF6,(2008), 525-530.
• 林守仁: 銅と銅合金, 48-1(2009), 245-248.
• ASTM standards: E399,(1990).
• 日本規格協会: JIS ハンドブック3非鉄 (2001).
• ASTM standards: E647-91,(1995).

Terms in the title (6)： 黄銅 ,  平板 ,  疲労き裂 ,  進展 ,  き裂先端 ,  変位