The effect of roll-processing orientation on stress corrosion cracking of warm-rolled 304L stainless steel in oxygenated and deoxygenated high temperature pure water

酸素化と脱酸素高温純水中の温間圧延304Lステンレス鋼の応力腐食割れに対する圧延加工方位の影響

Author (5)： LU Zhanpeng (Fracture and Reliability Res. Inst., Tohoku Univ., 6-6-01, Sendai 980-8579, JPN) ,  SHOJI Tetsuo (Fracture and Reliability Res. Inst., Tohoku Univ., 6-6-01, Sendai 980-8579, JPN) ,  DAN Tichun (Fracture and Reliability Res. Inst., Tohoku Univ., 6-6-01, Sendai 980-8579, JPN) ,  QIU Yubing (Fracture and Reliability Res. Inst., Tohoku Univ., 6-6-01, Sendai 980-8579, JPN) ,  YONEZAWA Toshio (Fracture and Reliability Res. Inst., Tohoku Univ., 6-6-01, Sendai 980-8579, JPN)
Material： Corrosion Science  (International Journal of the Science and Practice of Corrosion and Protection)
Volume： 52  Issue： 8  Page： 2547-2555  Publication year： Aug. 2010 
JST Material Number： B0135B  ISSN： 0010-938X  Document type： Article
Article type： 原著論文  Country of issue： United Kingdom (GBR)  Language： ENGLISH (EN)

Thesaurus term： *stress corrosion cracking ,  *austenitic stainless steel ,  rolling (plastic working) ,  *anisotropy ,  oxygenation ,  deoxidization ,  pure water ,  growth rate ,  grain boundary fracture ,  AISI 304L ,  warm rolling ,  *crack ,  *corrosion cracking

JST classification (2)： Corrosion  (WB03030B) ,  Rolling techniques  (WC06030Z)

Terms in the title (9)： 酸素化 ,  脱酸素 ,  純水 ,  温間圧延 ,  304L ,  ステンレス鋼 ,  応力腐食割れ ,  圧延 ,  加工方位