高輝度放射光CT法による腐食疲労損傷の発生と成長の観察

Author (2)： NAKAI YOSHIKAZU (神戸大) ,  SHIOZAWA DAIKI (神戸大)
Material： 検査技術  (Inspection Engineering (Tokyo))
Volume： 15  Issue： 8  Page： 1-7  Publication year： Aug. 01, 2010 
JST Material Number： L3524A  ISSN： 1342-9825  CODEN： KGEIAS  Document type： Article
Article type： 解説  Country of issue： Japan (JPN)  Language： JAPANESE (JA)

Thesaurus term： fatigue damage ,  *micro structure ,  synchrotron radiation facility ,  luminance ,  synchrotron radiation ,  beam line ,  tomographic image ,  morphology (form) ,  etch pit ,  fatigue crack growth ,  metal structure (microstructure) ,  in situ observation ,  contrast ,  passivation ,  passive state film ,  crack initiation ,  SPring-8 ,  high brightness ,  three-dimensional shape ,  *corrosion fatigue ,  computed tomography ,  organization ,  modification ,  conversion coating film ,  *fatigue ,  *Corrosion
Semi thesaurus term： *corrosion fatigue ,  computed tomography ,  fatigue crack ,  microstructure ,  CT image

JST classification (2)： Basic corrosion theory and corrosion test  (WB03020Q) ,  Metallography  (WB01010R)

Terms in the title (7)： 高輝度 ,  放射 ,  光CT ,  腐食疲労 ,  損傷 ,  成長 ,  観察