Study on FRACTURE TOUGHNESS of welded joints for heavy-thick steel plates by CENTRE-NOTCHED small size specimen

中心切欠き小型試験片による厚板鋼板の溶接継手の破壊靭性に関する研究

Author (6)： YAJIMA Hiroshi (Nagasaki Inst. Applied Sci., Nagasaki, JPN) ,  WATANABE Eiichi (Nagasaki Inst. Applied Sci., Nagasaki, JPN) ,  JIA Zi Meng (Nagasaki Inst. Applied Sci., Nagasaki, JPN) ,  YOSHIMOTO Kousuke (Nagasaki Inst. Applied Sci., Nagasaki, JPN) ,  ISHIKAWA Tadashi (Nippon Steel Corp., Chiba, JPN) ,  FUNATSU Yuuji (Nippon Steel Corp., Tokyo, JPN)
Material： Welding in the World  (Soudage dans le Monde)
Volume： 55  Issue： 5-6  Page： 84-92  Publication year： May. 2011 
JST Material Number： H0722A  ISSN： 0043-2288  Document type： Article
Article type： 原著論文  Country of issue： Germany, Federal Republic of (DEU)  Language： ENGLISH (EN)

Thesaurus term： *welded construction ,  large structure ,  container ship ,  steel plate ,  thick plate ,  *welded joint ,  *fracture toughness ,  fracture toughness test ,  test piece ,  small type ,  material testing ,  crack propagation ,  brittle fracture ,  butt welded joint ,  crack initiation ,  electrogas welding ,  length ,  size effect ,  sampling ,  stress intensity factor ,  fracture surface ,  temperature dependence ,  ductile-brittle transition ,  notch test ,  crack length ,  mechanical property
Semi thesaurus term： fatigue crack

JST classification (3)： Welding design,welded structures  (WC07140A) ,  Ship structure and materials  (QJ03020I) ,  Metallic materials  (HC04020L)

Terms in the title (7)： 切欠き ,  小型試験片 ,  厚板 ,  鋼板 ,  溶接継手 ,  破壊靭性 ,  研究