Copper Nanoparticles: Aqueous Phase Synthesis and Conductive Films Fabrication at Low Sintering Temperature

銅ナノ粒子 水溶液中合成と低焼結温度での導電膜製造

Author (5)： DENG Dunying (Fudan Univ., Shanghai, CHN) ,  JIN Yunxia (Fudan Univ., Shanghai, CHN) ,  CHENG Yuanrong (Fudan Univ., Shanghai, CHN) ,  QI Tianke (Fudan Univ., Shanghai, CHN) ,  XIAO Fei (Fudan Univ., Shanghai, CHN)
Material： ACS Applied Materials & Interfaces  (ACS Appl Mater Interfaces)
Volume： 5  Issue： 9  Page： 3839-3846  Publication year： May. 08, 2013 
JST Material Number： W2329A  ISSN： 1944-8244  CODEN： AAMICK  Document type： Article
Article type： 原著論文  Country of issue： United States (USA)  Language： ENGLISH (EN)

Thesaurus term： *carboxylic acid ,  *Copper ,  *nano particle ,  heating temperature ,  *thin film ,  *copper oxide ,  precursor (substance) ,  *hydrazine ,  reducing agent ,  thermogravimetric analysis ,  ink jet printing ,  aqueous solution ,  protectant ,  particle size distribution ,  *sintering ,  electric resistance ,  annealing (heat treatment) ,  amino acid ,  aliphatic amine ,  aliphatic carboxylic acid ,  primary amine ,  aliphatic alcohol ,  hydroxy acid ,  polycarboxylic acid ,  secondary alcohol ,  sintering temperature ,  passivation layer ,  *low temperature sintering
Semi thesaurus term： *conductive film

JST classification (1)： Conducting materials  (NA04020L)

Substance index (4)： Alanine ,  Citric acid ,  Glycolic acid ,  Lactic acid

Terms in the title (4)： 銅ナノ粒子 ,  水溶液 ,  焼結温度 ,  導電膜