EIS analysis of stress corrosion cracks propagation in 7003 aluminum alloy

7003アルミニウム合金の応力腐食割れ成長の電気化学インピーダンススペクトル解析【JST・京大機械翻訳】

Author (6)： Sun Bin (School of Materials Science and Engineering, Changzhou University, Jiangsu Key Laboratory of Materials Surface Science and Technology) ,  Song Renguo (School of Materials Science and Engineering, Changzhou University, Jiangsu Key Laboratory of Materials Surface Science and Technology) ,  Li Hai (School of Materials Science and Engineering, Changzhou University, Jiangsu Key Laboratory of Materials Surface Science and Technology) ,  Pan Shengdong (School of Materials Science and Engineering, Changzhou University, Jiangsu Key Laboratory of Materials Surface Science and Technology) ,  Wang Zhixiu (School of Materials Science and Engineering, Changzhou University, Jiangsu Key Laboratory of Materials Surface Science and Technology) ,  He Wangzhao (School of Materials Science and Engineering, Changzhou University, Jiangsu Key Laboratory of Materials Surface Science and Technology)
Material： Zhongguo Youse Jinshu Xuebao  (Chugoku Yushoku Kinzoku Gakuho)
Volume： 26  Issue： 9  Page： 1832-1842  Publication year： 2016 
JST Material Number： W0943A  ISSN： 1004-0609  CODEN： ZYJXFK  Document type： Article
Article type： 原著論文  Country of issue： China (CHN)  Language： CHINESE (ZH)

Abstract/Point： The slow strain rate test(SSRT...

Register(free) or Log In to access     To see more with JDream III (charged).   {{ this.onShowAbsJLink("http://jdream3.com/lp/jglobal/index.html?docNo=17A0172682&from=J-GLOBAL&jstjournalNo=W0943A") }}

Thesaurus term： aging (phenomenon) ,  *stress corrosion cracking ,  scanning electron microscope ,  *crack ,  *electrochemical impedance ,  particle size (ratio) ,  crack propagation ,  *spectral analysis ,  *impedance spectrum ,  *aluminum base alloy ,  stress strain curve ,  *stress corrosion ,  tensile test ,  mass fraction ,  electrochemical impedance spectrometry ,  *corrosion cracking ,  curve ,  line

Author keywords (5)： 7003 aluminum alloy ,  electrochemical impedance spectroscopy ,  stress corrosion cracks ,  initial crack ,  secondary crack

JST classification (3)： Secondary batteries  (YB04030K) ,  Electrochemical reaction  (CB07050F) ,  Corrosion prevention  (WB03040M)

Terms in the title (5)： アルミニウム合金 ,  応力腐食割れ ,  成長 ,  電気化学インピーダンス ,  スペクトル解析