Characterization of stress corrosion crack growth in austenitic stainless steel under variable loading in small- and large-scale yielding conditions

小規模および大規模降伏条件における可変荷重下のオーステナイトステンレス鋼における応力腐食割れ成長のキャラクタリゼーション【JST・京大機械翻訳】

Author (4)： Fujii Tomoyuki (Department of Mechanical Engineering, Shizuoka University, 3-5-1, Johoku, Naka-ku, Hamamatsu 432-8561, Japan) ,  Tohgo Keiichiro (Department of Mechanical Engineering, Shizuoka University, 3-5-1, Johoku, Naka-ku, Hamamatsu 432-8561, Japan) ,  Kawamori Motohiro (Department of Mechanical Engineering, Shizuoka University, 3-5-1, Johoku, Naka-ku, Hamamatsu 432-8561, Japan) ,  Shimamura Yoshinobu (Department of Mechanical Engineering, Shizuoka University, 3-5-1, Johoku, Naka-ku, Hamamatsu 432-8561, Japan)
Material： Engineering Fracture Mechanics  (Eng Fract Mech)
Volume： 205  Page： 94-107  Publication year： 2019 
JST Material Number： A0119A  ISSN： 0013-7944  Document type： Article
Article type： 原著論文  Country of issue： United Kingdom (GBR)  Language： ENGLISH (EN)

Abstract/Point： To investigate the factors tha...

Register(free) or Log In to access     To see more with JDream III (charged).   {{ this.onShowAbsJLink("http://jdream3.com/lp/jglobal/index.html?docNo=19A0069255&from=J-GLOBAL&jstjournalNo=A0119A") }}

Thesaurus term： *austenitic stainless steel ,  *variable load ,  crack propagation ,  stress intensity factor ,  *characterization ,  *stress corrosion cracking ,  J integral ,  crack growth rate ,  SUS 304 ,  *yielding condition ,  *crack ,  *corrosion cracking

Author keywords (5)： Stress corrosion cracking ,  Crack growth ,  Fracture mechanics ,  Stress intensity factor ,  J integral

JST classification (1)： Metallic materials  (HC04020L)

Terms in the title (7)： 大規模 ,  降伏条件 ,  可変荷重 ,  オーステナイトステンレス鋼 ,  応力腐食割れ ,  成長 ,  キャラクタリゼーション